Figure 1 Trigonal dodecahedral oxygen environment of the La3+ cation in defect scheelite-type La0.667[MoO4]; ellipsoids are drawn at the 80% probability level. [Symmetry codes: (i) x, y, z; (ii) -x + [{1\over 2}], -y, z + [{1\over 2}]; (iii) -y + [{3\over 4}], x + [{1\over 4}], z + [{1\over 4}]; (iv) y + [{3\over 4}], -x + [{3\over 4}], z + [{3\over 4}]; (v) -x, -y, -z; (vi) x + [{1\over 2}], y, -z + [{1\over 2}]; (vii) y + [{1\over 4}], -x + [{3\over 4}], -z + [{3\over 4}]; (viii) -y + [{1\over 4}], x + [{1\over 4}], -z + [{1\over 4}]].  [article HTML]