Figure 6
Dependence of the diffraction contrast on absorption for rod-like defects in SLG crystals. Transmission projection topographs of sample B [region F marked in Fig. 1[link](d)]. (a) Lang topograph; (b), (c) synchrotron white-beam topographs. I1(2) is the intensity of the type 1 (2) wavefield, I0 is the initial value of intensity; I1(2) = I0exp[-[mu]1(2)t], where t is the thickness of the sample.  [article HTML]