![[Figure 2]](wh5004fig2mag.jpg)
|
|
Figure 2
Powder X-ray diffraction patterns from the Zn2V2O7–Mn2V2O7 pseudobinary system for compositions of the general form (Zn1 − xMnx)2V2O7. Values of x are shown on the left-hand side above each diffraction pattern. Peaks for x = 0.05 and 0.1 are from the α-Zn2V2O7 solid solution in which manganese substitutes for zinc (Krasnenko et al., 2002a  ,b). Peaks for x = 0.25 and 0.3 are from the pure L phase, while for x = 0.15 and 0.2 the peaks evident in the X-ray diffraction patterns are from both the α-Zn2V2O7 solid solution and the L phase. |
![[Figure 2]](wh5004fig2.jpg)