The asterism observed in white radiation X-ray diffraction images (topographs) of extended cracks in silicon is investigated and found to be associated with material that is close to breakout and surrounded by extensive cracking. It is a measure of the mechanical damage occurring when the fracture planes do not follow the low-index cleavage planes associated with the crystal structure. It is not related to a propensity for some cracked wafers to shatter during subsequent high-temperature processing. There is no correlation between crack morphology and alignment of an indenter with respect to the orientation of a silicon wafer, the cracks being generated from the apices of the indenter and having threefold symmetry for Berkovich indents and fourfold symmetry for Vickers indents. X-ray diffraction imaging (XRDI) of indents does not reveal this underlying symmetry and the images exhibit a very substantial degree of variation in their extent. This arises because the XRDI contrast is sensitive to the long-range strain field around the indent and breakout reduces the extent of this long-range strain field. Breakout is also detected in the loss of symmetry in the short-range strain field imaged by scanning micro-Raman spectroscopy. Weak fourfold symmetric features at the extremes of the images, and lying along 〈110〉 directions, are discussed in the context of slip generated below the room-temperature indents. Scanning electron microscopy imaging of the region around an indent during focused ion beam milling has permitted the three-dimensional reconstruction of the crack morphology. The surface-breaking Palmqvist cracks are found to be directly connected to the median subsurface cracks, and the presence of extensive lateral cracks is a prerequisite for material breakout at indenter loads above 200 mN. The overall crack shape agrees with that predicted from simulation.

Subscribe to Journal of Applied Crystallography

The full text of this article is available to subscribers to the journal.

If you have already registered and are using a computer listed in your registration details, please email support@iucr.org for assistance.

Buy online

You may purchase this article in PDF and/or HTML formats. For purchasers in the European Community who do not have a VAT number, VAT will be added at the local rate. Payments to the IUCr are handled by WorldPay, who will accept payment by credit card in several currencies. To purchase the article, please complete the form below (fields marked * are required), and then click on `Continue'.
E-mail address* 
Repeat e-mail address* 
(for error checking) 

Format*   PDF (US $40)
   HTML (US $40)
   PDF+HTML (US $50)
In order for VAT to be shown for your country javascript needs to be enabled.

VAT number 
(non-UK EC countries only) 
Country* 
 

Terms and conditions of use
Contact us

Follow J. Appl. Cryst.
Sign up for e-alerts
Follow J. Appl. Cryst. on Twitter
Follow us on facebook
Sign up for RSS feeds