research papers
| STRUCTURAL SCIENCE CRYSTAL ENGINEERING MATERIALS |
accessK0.72Na1.71Ca5.79Si6O19 – the first oligosilicate based on [Si6O19]-hexamers and its stability compared to cyclosilicates
aInstitute of Mineralogy and Petrography, University of Innsbruck, Innrain 52, 6020 Innsbruck, Austria, bDepartment of Mineralogy and Crystallography, University of Vienna, Josef-Holaubek-Platz 2, A-1090 Vienna, Austria, and cDepartment of General, Inorganic and Theoretical Chemistry, University of Innsbruck, Innrain 80-82, A-6020 Innsbruck, Austria
*Correspondence e-mail: volker.kahlenberg@uibk.ac.at
Synthesis experiments were conducted in the quaternary system K2O–Na2O–CaO–SiO2, resulting in the formation of a previously unknown compound with the composition K0.72Na1.71Ca5.79Si6O19. Single crystals of sufficient size and quality were recovered from a starting mixture with a K2O:Na2O:CaO:SiO2 molar ratio of 1.5:0.5:2:3. The mixture was confined in a closed platinum tube and slowly cooled from 1150°C at a rate of 0.1°C min−1 to 700°C before being finally quenched in air. The structure has tetragonal symmetry and belongs to P4122 (No. 91), with a = 7.3659 (2), c = 32.2318 (18) Å, V = 1748.78 (12) Å3, and Z = 4. The silicate anion consists of highly puckered, unbranched six-membered oligomers with the composition [Si6O19] and symmetry 2 (C2). Although several thousands of natural and synthetic oxosilicates have been structurally characterized, this compound is the first representative of a catena-hexasilicate anion, to the best of our knowledge. Structural investigations were completed using Raman spectroscopy. The spectroscopic data was interpreted and the bands were assigned to certain vibrational species with the support of density functional theory at the HSEsol level of theory. To determine the stability properties of the novel oligosilicate compared to those of the chemically and structurally similar cyclosilicate combeite, we calculated the of the respective structures using the equalization method. The results showed that the molecular of the cyclosilicate was significantly higher than that of the oligostructure due to the different connectivities of the oxygen atoms within the molecular units.
Keywords: crystal structure; oligosilicate; [Si6O19] unit; electronegativity equalization method; K0.72Na1.71Ca5.79Si6O19.
CCDC reference: 2372966
1. Introduction
This paper presents a study on a new phase of the quaternary system K2O–Na2O–CaO–SiO2. Crystalline compounds and subsolidus equilibria in the Na2O–CaO–SiO2 and K2O–CaO–SiO2 subsystems have been frequently investigated in the past (Kahlenberg & Hösch, 2002![[Kahlenberg, V. & Hösch, A. (2002). Z. Kristallogr. 217, 155-163.]](../../../../../../logos/arrows/b_arr.gif "Kahlenberg, V. & Hösch, A. (2002). Z. Kristallogr. 217, 155-163."){kind=small}
; Kahlenberg et al., 2010; Arroyabe & Kahlenberg, 2011; Schmidmair et al., 2017; Schmidmair et al., 2018). However, recent studies have described several new silicates containing calcium as well as sodium or potassium, such as γ-Na2Ca6Si4O15 or K4CaSi6O15 (Kahlenberg et al., 2022; Liu et al., 2021). This suggests that these systems are not yet as well understood as one might expect. In contrast, the quaternary system containing both alkali oxides remains largely unexplored, and detailed thermodynamic or phase analysis data are not yet available.
In silicate glass research, it has been long recognized that the simultaneous presence of both Na+ and K+ cations in the melt and the resulting glasses can cause significant changes in certain physicochemical properties (Dilmore et al., 1978; Grund & Jonson, 2009). This phenomenon known as the mixed alkali effect describes how chemical durability, and viscosity can vary in an extremely nonlinear fashion when one alkali oxide is gradually substituted by another (Shelby, 2005).
To date, only a limited number of potassium–sodium–calcium silicates have been structurally characterized, such as K1.08Na0.92Ca6Si4O15 (Kahlenberg et al., 2018a), Na1.5K0.5Ca6Si4O15 (Kahlenberg et al., 2018b), and NaKCa4[Si9O23] (Kasatkin et al., 2019). The first two members are mixed-anion silicates and are isostructural with phases of the ternary subsystems. The third compound, corresponding to the mineral patynite, has a previously unknown structure type and belongs to the group of inosilicates based on branched tubular [Si9O23]10− chains. Additionally, there are indications that combeite (ideally Na4Ca4Si6O18) can incorporate small amounts of potassium (Kahlenberg, 2023). The example of patynite emphasizes the need for a more thorough analysis of the quaternary system Na2O–K2O–CaO–SiO2. It suggests that additional phases may exist, which are not mere solid solutions of end members containing only one alkali cation species. Knowledge of the existence of novel Na–K–Ca silicates is also important for thermodynamic modelling of the system using program packages such as FactSage (Bale et al., 2009). This understanding is crucial for comprehending the processes that occur in slags from biomass combustion (Vassilev et al., 2013; Santoso et al., 2020).
In addition to diffraction-based structure investigations, a deeper understanding of crystalline materials can be achieved by computing key physicochemical properties through quantum chemical calculation methods such as density functional theory (DFT) (Argaman & Makov, 2000; Brink, 2002; Jones, 2015; Yu et al., 2016). This method represents a well established theoretical framework for characterizing chemical systems and has been increasingly successful (Becke, 2014; Schleder et al., 2019). However, quantum mechanical approaches have the disadvantage of high computational costs that increase unfavourably with system size. If the research question is based on a basic estimation of crystalline properties, such as χ or charge distribution, alternative techniques have been developed that avoid a full quantum mechanical treatment. χ is a particularly suitable parameter that has been used, among others, to characterize and distinguish different silicate-based solid-state systems. This chemical property provides initial information about the charge transfer effects, and thus about the structural stability of materials (Shankar & Parr, 1985). The electronegativity equalization method (EEM) (Mortier et al., 1985; Mortier et al., 1986) is a simple parameterized framework that estimates the molecular χmol associated with the partial charge distribution in the system.
Previous investigations of silica structures (including real and hypothetical zeolites with SiO2 composition) have shown that the EEM approach can be applied to predict the stability of SiO2 polymorphs in a simple and effective way (Van Genechten et al., 1987; Van Genechten & Mortier, 1988; Janssens et al., 1995; Verstraelen et al., 2012). In this work, an adaptation of the elementary EEM approach has been introduced by using the shielded EEM scheme of the reaction force-field (ReaxFF) method, which allows the extension of this method to more complex silicate systems. The ReaxFF method originates from the molecular dynamic field and has been used for various solid-state characterizations (Senftle et al., 2016; Leven et al., 2021). For our specific case, this EEM advancement was positively verified by comparing it with the results of previous investigations on SiO2 modifications (Henry, 1997) and Van Genechten et al. (1987). Thus, the ReaxFF parameters (Joshi et al., 2014) and our scheme have been shown to provide the same stability trend as proposed in the literature when applied to binary SiO2 systems.
This validated EEM approach was used to gain some insight into the stability differences between the exotic hexameric [Si6O19] oligomer present in the compound under investigation (K0.72Na1.71Ca5.79Si6O19) and the much more frequent six-membered [Si6O18] rings existing, for example, in the chemically and structurally related mineral combeite (ideally Na4Ca4[Si6O18]; Fischer & Tillmanns, 1987). In addition, the experimentally determined Raman spectra were interpreted with the aid of a harmonic vibrational analysis (Ozaki et al., 2021; Wolters & Braun, 2018) conducted at the HSEsol level of theory (Schimka et al., 2011).
2. Experimental and computational details
2.1. Synthesis
For the synthesis experiment, the molar ratio of K2O:Na2O:CaO:SiO2 was 1.5:0.5:2:3. Na2CO3 (Merck, 99.9%), CaCO3 (Merck, >99.9%), K2CO3 (Alfa Aesar, 99.997%) and SiO2 (AlfaAesar, 99.995%) were dried for 24 h at 400°C before being weighed on an analytical balance. Subsequently, a 2 g batch corresponding to the aforementioned molar ratio was thoroughly mixed in a planetary ball mill for 45 min at 600 rpm using ethanol as a grinding fluid. After evaporating the alcohol at 50°C in a hot-air cabinet, the reactants were stored in a desiccator. The high-temperature treatment was carried out in a small platinum capsule with an inner diameter of 5 mm and a length of approximately 35 mm. The lower end of the capsule was closed using a welding apparatus, and 72.8 mg of the reactant mixture was charged into the container. A sintered corundum combustion boat was filled with hollow spheres of alumina, and the capsule was placed vertically inside. The boat was then transferred to a resistant heated chamber furnace and slowly heated from ambient temperature to 700°C. After annealing for 67 h to ensure complete disintegration of the carbonates the sample was removed from the furnace. The observed weight loss corresponded to the expected value for the release of CO2. Finally, the upper open end of the capsule was pinched and welded shut. Sealing was performed to prevent evaporation of K2O and Na2O, which is likely to occur at elevated temperatures. The capsule was then heated from 140°C to 1150°C with a ramp of 5°C min−1. After holding the target temperature for 1.5 h, the sample was cooled down to 700°C with a rate of 0.1°C min−1 and, finally, quenched in air to ambient conditions by removing the alumina container from the furnace. The closed capsule was weighed before and after the high-temperature treatment. No weight loss was observed, indicating that the container remained intact throughout the synthesis process.
2.2. Single-crystal X-ray diffraction
After opening the Pt capsule with a micropincer, the solidified material was transferred to a glass slide and further checked using polarization microscopy. The material was found to consist of transparent, colourless birefringent crystals up to 150 µm in diameter and a glassy isotropic matrix showing conchoidal fracture. The crystals exhibited very good optical quality, displaying a sharp extinction between crossed polarisers. Fifteen crystals were affixed to the tips of glass fibres using nail polish. The crystals were then studied using single-crystal diffraction performed on an Oxford Diffraction Gemini R Ultra diffractometer, which was equipped with a four-circle kappa-goniometer and a Ruby CCD detector. Preliminary diffraction experiments aimed at the determination of the unit-cell parameters and revealed the presence of three different phases: rankinite (Ca3Si2O7), wollastonite (CaSiO3), and an unidentified compound with a tetragonal metric that did not match any entries contained in the current version of the Inorganic Database (Hellenbrandt, 2004). Hence, the most superior diffraction quality sample of the novel compound was chosen for further structure analysis. A full sphere of reflections up to 26.37 °θ was obtained using Mo Kα radiation (refer to Table 1). The data was processed using the CrysAlis PRO software package (Rigaku Oxford Diffraction, 2020). Following indexing, the diffraction pattern was integrated. The data reduction process involved incorporating as well as applying an analytical numeric absorption correction using a multifaceted crystal model.
|
The intensity statistics did not provide a clear indication of the presence or absence of a centre of symmetry. Merging the data set in the two potential tetragonal Laue groups 4/m and 4/mmm resulted in almost identical internal R values. Therefore, it was assumed that the diffraction symmetry corresponds to the holosymmetric Based on the observed (00l): l = 4n, only the two enantiomorphic space groups P4122 and P4322 remained. The structure solution was successfully initiated in P4122 using (SIR2002; Burla et al., 2003), which provided a crystal-chemically reasonable starting model. Some missing oxygen atoms were found from a difference Fourier map (SHEXL97; Sheldrick, 2015). The same software was also employed for subsequent full-matrix least-squares refinements. The scattering curves and coefficients were obtained from the International Tables for Crystallography, Vol. C (Prince, 2004). Section 3 will provide a detailed analysis of the site populations of the seven non-tetrahedrally coordinated cation sites in the The resulting chemical composition from the structure analysis was K0.72Na1.71Ca5.79Si6O19. The correctness of the was indicated by a value of −0.03 (5) for the (Flack, 1983). Table 2 provides the final coordinates, site occupancies, and equivalent isotropic displacement parameters, while Table 3 lists the anisotropic displacement parameters. Table 4 summarizes the selected interatomic distances. Structural features were illustrated using VESTA3 program (Momma & Izumi, 2011). Bond valence sum calculations have been performed using the parameter sets of Brown & Altermatt (1985) for Ca–O, K–O and Na–O interactions as well as Brese & O'Keeffe (1991) for the Si—O bonds (see Table 2).
| ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
2.3. Chemical analysis
The crystal that has been used for structural investigations was removed from the glass fibre and studied using wavelength-dispersive (WDS) analysis using a Jeol Superprobe JXA-iSP100 electron beam microprobe. The nail polish was dissolved with acetone and the crystal was thoroughly cleaned with a drop of water. The crystal was then mounted directly on an aluminium sample holder without any polishing using a small amount of a hot-melt adhesive, and finally coated with carbon. The acceleration voltage was 15 kV and the beam current was 10 nA. The counting times on the peaks were 20 s, with half that time on both sides of the peaks. The average results for three different spots, when normalized to 19 oxygen atoms, are as follows: K0.81 (5)Na1.50 (5)Ca5.69 (3)Si6.08 (4)O19. The analysis confirms the simultaneous presence of Na, K and Ca, but the resulting stoichiometry differs slightly from that of the structure The observed differences may be attributed to the fact that the crystal was measured in its natural state, without any polishing. Regrettably, the crystal was lost while attempting to embed it in epoxy resin for a second analysis run with a better surface finish. Taking into account the non-ideal conditions of the electron beam microprobe measurements, we consider the agreement between direct WDS and indirect single-crystal X-ray diffraction (SCXRD) chemical analyses to be satisfactory. It should be noted that the silicate glass phase present in the sample has not been analysed. However, it is reasonable to assume that it is enriched in Na2O and especially K2O in relation to the alkali-free crystalline byproducts observed in the SCXRD screening process.
2.4. Raman spectroscopy
Raman spectra were collected at the University of Vienna using a Renishaw RM1000 confocal edge filter-based micro-Raman system. The sample analysed was a randomly oriented single crystal of K0.72Na1.71Ca5.79Si6O19 embedded in nail polish for transport. The sample surface was excited with the blue 488 nm (20 mW) emission line of an Ar+ laser using a 50×/0.75 objective lens. The back-scattered radiation (180° configuration) was analysed with a 1200 lines per mm grating monochromator. Unpolarized Raman intensities were collected using a thermo-electrically cooled CCD array detector for 300 s in static grating mode, covering a spectral range of approximately 70 to 1680 cm−1. To obtain the final spectrum, faint signals of the nail polish were subtracted. The system has a spectral resolution of 5–6 cm−1 and a wavenumber accuracy of 1 cm−1, both calibrated with the Rayleigh line and the 521 cm−1 line of a Si standard. The confocal setup limited the spatial resolution (both lateral and in depth) to 2−3 µm. Instrument control and data acquisition were performed using the Grams/32 software (Galactic Ind. Corp.). Fig. 1 shows the Raman spectrum of the compound under investigation.
![[Figure 1]](dk5130fig1thm.gif) | Figure 1 Unpolarized Raman spectrum of a single crystal of K0.72Na1.71Ca5.79Si6O19. |
2.5. Theoretical calculations
In order to investigate the stability of K0.72Na1.71Ca5.79[Si6O19], the EEM approach is applied by using our in-house developed EEM framework. A detailed theoretical overview of the used EEM approach can be found in Appendix A. Furthermore, a validation of the approach using a set of test silica structures, is provided in Appendix B. Section 3.1 will discuss the present oligosilicate K0.72Na1.71Ca5.79[Si6O19], which contains cation sites with mixed or partial site occupancies. This feature is also observed in the cyclosilicate combeite, which was chosen as a benchmark to compare the stability of open hexameric oligomers and closed six-membered silicate rings.
Many silicate structures involve cation substitutions on the non-tetrahedral positions. Unfortunately, this cannot be reproduced in a computational structure model. In order to model mixed occupancies, it is necessary to apply an order of magnitude of the size, which is very difficult to achieve or indeed beyond the accessible scope of using DFT for structure optimization.
Therefore, reasonably idealized site occupations were employed. Consequently, this work used structural models that considered either full potassium or full sodium occupation, which represent idealized structural models. Regardless of the different occupations of the monovalent ionic sites, the population of the calcium positions remained unchanged. To facilitate the EEM calculation framework, trigonal combeite was transformed into an orthogonal as illustrated in Fig. 2. The EEM parameter sets used for the different elements are listed in Table 5.
| ||||||||||||||||||||||||||||||
![[Figure 2]](dk5130fig2thm.gif) | Figure 2 Workflow for generating the model structures for the theoretical calculations. Experimentally determined mixed K–Na occupancies were idealized to either fully populated K or Na sites. Orthogonal supercells were used for the EEM calculations (refer to Table 5 ). The labels `Na' and `K' indicate the species considered as the monovalent cation in the corresponding systems. The assignments of the calcium atoms in both the cyclo- and the oligosilicate remained unaltered. |
Although the calculated structural model differs from the experimentally found K0.72Na1.71Ca5.79[Si6O19] oligosilicate, the conclusion of the stability study can be considered consistent due to the non-idealized occupancies in the oligosilicate and cyclosilicate combeite. The objective of the EEM calculations is to investigate the stability of K0.72Na1.71Ca5.79[Si6O19] oligosilicate in comparison to the cyclosilicate combeite, with a particular focus on their differing silicate anions. The effects of different crystal structures on their stability have been demonstrated using various SiO2 polymorphs as test structures, see Figs. S2 and S3 in the supporting information.
In addition, the study compared the optimized and non-optimized structures to assess the effect of structure optimization, carried out using the same computational settings as in the validation test, see Appendix B. The initial calculations for the different SiO2 test structures described above (see supporting information, Fig. S1), showed that the results obtained using the two different basis sets, pob-DZVP-rev2 and pob-TZVP-rev2 (Vilela Oliveira et al., 2019), were sufficiently identical (see supporting information, Fig. S2). However, the latter basis set was not used for the calculations of the oligo- and the cyclosilicate due to its increased computational requirements. To further characterize the idealized oligosilicate, an in-silico vibrational analysis (infrared and Raman) was carried out using the program Crystal23 (Erba et al., 2023) at the minimum geometry calculated within the harmonic approximation (Ozaki et al., 2021). The theoretical line spectra were then subjected to a weighted kernel density estimation using a Gaussian kernel with a width of 2.5 × 10−3 cm−1 to allow comparison with the experimental spectral data (Wolters & Braun, 2018). The calculated Raman spectra were then compared to the measured values, taking into account both parallel and perpendicular polarization, as well as the respective total intensity as obtained from Crystal23.
3. Results
3.1. Description of the crystal structure
The of K0.72Na1.71Ca5.79Si6O19 is primarily composed of silicate polyanions. These polyanions are formed by the non-cyclic condensation of six [SiO4] tetrahedra. According to Liebau's silicate compendium (Liebau, 1985), the resulting [Si6O19] units can be identified as a group of unbranched sixfold tetrahedra. Oligoanions with multiplicities m greater than three are uncommon among the numerous natural and synthetic silicate structures that have been determined (Liebau, 1985). The phase studied in this contribution is the first example of an oligosilicate with m = 6. The hexamer present in K0.72Na1.71Ca5.79Si6O19 is not linear, as shown in Fig. 3(a), but exhibits a high degree of corrugation. The six silicon cations of a single group are located at the corners of an imaginary distorted cube with edge lengths between 3.22 and 4.60 Å. The symmetry of a single cluster is 2 (or C2) [see Fig. 3(b)]. Due to the specific type of connectivity, four tetrahedra exhibit two bridging oxygen atoms (Obr), while the remaining two [SiO4] moieties at the open ends show only one Obr each. The individual Si—O bond distances vary considerably, as shown in Table 4 (ranging from 1.590 to 1.645 Å). However, the obtained values fall within the normal range for oxosilicate structures and their variations follow expected trends. The bond distances between silicon and the bridging oxygen atoms (O8, O9, O10) are consistently longer than the non-bridging Si—O bonds for all three crystallographically independent tetrahedral units. Their deviation from the ideal ![[{\bar 4}3m]](teximages/dk5130fi1.svg){kind=small}
symmetry is also reflected in the Si—O—Si angles, which range from 102 to 119° (refer to Table 6). The distortion can be quantified numerically using the quadratic elongation (QE) and the angle variance (AV) as defined by Robinson et al. (1971). The corresponding values for the tetrahedra are presented in Table 4. The conformation of the hexamer can be conveniently expressed using the three torsion angles defined by four successive Si atoms along the group. These values are also listed in Table 6.
| ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
![[Figure 3]](dk5130fig3thm.gif){kind=small} | Figure 3 Side views of a single [Si6O19] oligoanion. (a) The six Si atoms occupy the corners of a distorted cube, with the remaining two corners occupied by M1 cations. (b) A single [Si6O19]-cluster has symmetry 2 (or C2). (c) The corresponding distorted cube in combeite, ideally Na4Ca4Si6O18, contains a cyclic [Si6O18] ring. The oxygen and silicon atoms are shown in red and blue, respectively. M1 corresponds to a mixed site occupied by calcium (light blue) and sodium (yellow) cations. The sizes of the two-coloured segments refer to the percentages determined from the site-occupancy refinements. |
The Na, K and Ca ions within the must compensate for the 56 negative charges of the silicate anions. The three cation species distribute among seven non-tetrahedrally coordinated positions having six (M1), seven (M2), eight (M3, M4, M5, M7), and ten (M6) next oxygen neighbours. The around M1 can be described as a distorted octahedron, whereas the polyhedra around the remaining M positions are more complex. Based on the bond distance analysis, it is concluded that M1–M5 are mixed Na/Ca positions, whereas M7 corresponds to a potassium site. Table 2 shows the results of an unconstrained of the individual site occupancies for these six positions. As a result, M1–M4 are dominated by Ca, while M5 contains significant amounts of both Ca and Na. The occupancy of the M7 position is only partial. In total, these six sites represent 50.01 (6) charges per cell. Therefore, the remaining M6 position must provide another six positive charges to achieve electroneutrality. It is worth noting that the observed scattering density on the M6 position amounts to almost exactly 18 electrons which is compatible with both K+ and Ca2+. Occupancy refinements based on laboratory diffraction data are usually unable to directly access mixed site populations containing isoelectronic cations. This is due to the limitation of using only one fixed wavelength, which usually impedes the targeted exploitation of effects to enhance the scattering contrast between the two ions. In this particular case, there is only one possible solution to achieve the six missing charges. The M6 site – a special position with a multiplicity of four – must be equally populated with Ca and K, resulting in a 1:1 ratio. Bond valence sum calculations provide additional evidence for the mixed K/Ca occupancy of M6. These calculations allow for an independent, though usually rather rough estimate of the contents of two different atom types sharing the same position (Brown, 2016). The concentrations obtained using the bond valence parameters of Brown & Altermatt (1985) for the K–O and Ca–O interactions in combination with the M6—O bond distances given in Table 4 are as follows: 62% K and 38% Ca. This result is considered to compare well with the percentages determined from charge neutrality requirements. The chemical composition, when normalized for 19 oxygen atoms per formula unit (a.p.f.u.) can be expressed as K0.72Na1.71Ca5.79Si6O19. This formula compares well with the one obtained by WDS analysis.
Fig. 4 shows the arrangement of the of the sites M2–M7. The six positions are located at the corners (M3), as well as the centres of edges (M2, M4, M6) and faces (M5, M7) of pseudocubic modules (tetragonal prisms). The total contains four of these modules. The dimensions of unit-cell parameters directly reflect the edge lengths of the modules, where a′ is equal to a and b, while c is approximately 4 × a′. The cation site M1, which is octahedrally coordinated, is located at the remaining two opposite corners of the smaller cubes defined by the six Si atoms belonging to a single hexamer [refer to Fig. 3(a)]. These smaller cubes occupy the barycenters of the larger pseudocubic modules (refer to Fig. 5). The entire contains four of the cube-in-cube modules that are stacked by applying the 41-screw axis running parallel to [001] (refer to Fig. 6).
![[Figure 4]](dk5130fig4thm.gif) | Figure 4 The non-tetrahedral cation positions M2–M7 occupy the corners (M3), the edge centres (M2, M4, M6) as well as the face centres (M5, M7) of pseudocubic modules (tetragonal prisms). The cations are potassium (violet), sodium (yellow) and calcium (light blue). The sizes of the bi-coloured segments indicate the percentages determined from the site-occupancy refinements. Note that M7 is only partially occupied. |
![[Figure 5]](dk5130fig5thm.gif) | Figure 5 This is a single cube-in-cube arrangement, whereby the smaller distorted cube is defined by the six silicon atoms of the [Si6O19] unit, in addition to two M1 cations. This cube is situated at the centre of an even larger cube, which is defined by the remaining M positions. |
![[Figure 6]](dk5130fig6thm.gif) | Figure 6 Stacking of four cube-in-cube unit cell defining modules by a 41-screw axis running parallel to [001]. |
3.2. Topological aspects
The can be understood differently as a mixed tetrahedral–octahedral framework based on [SiO4] and [M1O6] units, which contains voids of various sizes that host the remaining Na, Ca and K ions. The mixed framework has been topologically characterized in detail, including coordination sequences and extended point symbols, using the program ToposPro (Blatov et al., 2014). Therefore, the framework is represented by a graph consisting of vertices (T sites containing Si1, Si2 and Si3, M1 site as well as O atoms) and edges (bonds) connecting them. The nodes of the graph can be classified based on their coordination sequences {Nk} (Blatov, 2012), which is a set of integers {Nk} (k = 1,..,n), representing the number of sites in the k-th coordination sphere of the T/M or O atom selected as the central one. Table 7 summarizes the corresponding values for the symmetrically independent T sites and the M1 position up to n = 12. Additionally, the extended point symbols (Blatov et al., 2010) that list all shortest circuits for each angle for any non-equivalent framework atom have been determined and are also provided in Table 7. Finally, the polyhedral micro-ensembles or PMEs have been constructed (see Fig. 7). On the lowest sublevel they are formed for each octahedron and tetrahedron in the by considering all directly bonded [M1O6] and [SiO4] groups. They represent a geometric interpretation of the coordination sequences up to the index k = 3. The PMEs of the first sublevel observed for the M1 nodes can be described as follows: each [M1O6] octahedron is immediately linked to six tetrahedra. The M1 PME can be denoted as {6,6,18} using the classification based on the calculation of the coordination sequences up to k = 3 (Ilyushin & Blatov, 2002). The PMEs of the three crystallographically independent tetrahedral Si nodes conform to {4,4,16} (for Si1), {4,3,11} (for Si2), and {4,4,18} (for Si3) [refer to Figs. 7(a) to 7(d)].
| ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
![[Figure 7]](dk5130fig7thm.gif) | Figure 7 Polyhedral micro-ensembles of the crystallographically independent octahedral (M1) and tetrahedral (Si) nodes: (a) {6,6,18} (for M1), (b) {4,4,16} (for Si1), (c) {4,3,11} (for Si2) and (d) {4,4,18} (for Si3). |
3.3. Raman spectroscopy
As the present compound is the first example of a silicate based on [Si6O19] units, there are no other spectroscopic data available for crystalline materials based on this moiety in the literature. However, Raman spectra for chemically related oligosilicates with [Si3O10] units, such as K2Ca3Si3O10 (Arroyabe et al., 2011), have been reported. The band assignments of these authors can be helpful for interpreting the basic features of the spectrum of K0.72Na1.71Ca5.79Si6O19. Fig. 1 shows the experimental Raman spectrum, which displays at least 12 bands. The modes above about 800 cm−1 are typically attributed to Si—O stretching vibrations of the [SiO4] tetrahedra within the larger oligomers, while those in the range between 350 cm−1 and 800 cm−1 are assigned to O—Si—O and Si—O—Si bending vibrations. The modes within the low-frequency range (< 350 cm−1) correspond to (Na,K,Ca)–O vibrations. Fig. 8 presents a comparison between the calculated Raman spectra and their experimental counterparts. Table S3 summarizes the numerical data. Comparison between the perpendicular and parallel contributions of the total Raman spectral patterns exhibits the same bands with effectively the same intensities. The main experimental bands are located in the region between 1016 cm−1 and 875 cm−1. The calculated bands exhibit minor deviations of a few wavenumbers, while the intensities are significantly lower than the experimental data. The experimental results display several sidebands with much lower intensity in the 649 cm−1 to 109 cm−1 region. Despite the reduced intensity, the calculated bands are in good agreement with the experimental reference. The observed differences can be attributed to four factors. First, the non-tetrahedral cation sites are only partially occupied, which cannot be reflected in the harmonic frequency calculation. Second, the use of an energy-minimized structure inherently involves a 0 K treatment, which only allows for a relative measure of stability. Third, experimental Raman intensities are strongly contingent upon the laser wavelength, the sensitivity curve of the used CCD detector, the transmittance of the grating, and other optical components of the system. Finally, the crystal was not of gem quality and may have contained inclusions of the other two phases that crystallized concurrently.
![[Figure 8]](dk5130fig8thm.gif) | Figure 8 Comparison of the measured and calculated Raman spectra of the oligosilicate is presented. The calculated spectra are separated into contributions associated with parallel and perpendicular polarization as well as for the total intensity, as obtained from the output of the program Crystal23. The left-hand side shows the complete spectra, while the right-hand side presents a close-up of the main silicate stretching bands. |
3.4. EEM calculations
In addition to calculating harmonic frequencies, we estimated molecular electronegativities using the EEM method. In Fig. S3, EEM validation results based on various silica structures can be found. The results show that the adjusted EEM approach can accurately replicate the sequence of the molecular values χmol of chemically simple SiO2 polymorphs, such as α-cristobalite, α-quartz, coesite and stishovite, as previously reported by Henry (1997) and Van Genechten et al. (1987), respectively. In this study, it was observed that increases with increasing unit-cell volume and it converges towards a constant value as expected from the EEM approach (refer to Fig. S2). The optimal size for achieving balance between accuracy and computational costs is approximately 40 Å. Furthermore, it is important to consider the size as isotropic as possible to avoid any artefacts caused by anisotropic orientation. This will ensure a spatially consistent treatment of the radially symmetric Coulomb interactions that contribute to the potential considered in the EEM approach [refer to equation (5), Appendix A]. Table 8 provides the optimal trade-off between an isotropic and an appropriate unit-cell size to reach at least the plateau area of the molecular χmol for both the oligo- and the cyclosilicate. It summarizes the parameters of the orthogonal geometry-optimized supercells that were constructed using the primitive unit cells obtained via energy minimization of the structure, including the lattice parameters, at the HSESol / pob-DZVP-rev2 level of theory. As the pob-TZVP-rev2 and pob-DZVP-rev2 bases effectively yielded the same structural parameters, the latter was deemed sufficient for this work.
| |||||||||||||||||||||||||||||||||||||
Fig. 9 displays the charge distributions of the experimental (a) and optimized (b) structures resulting from the EEM calculations. The experimental structures exhibit similar results with respect to their geometry optimized counterparts. The comparison shows that the charge patterns are in good agreement with each other, with only minor shifts in the individual charge distributions. However, the charge distribution shape is broader in the experimental geometry than in the respective optimized structure. On the other hand, the charge patterns for the experimental cyclosilicate with Na and K occupation are very similar, with only a small shift being visible in the Na and K charge distribution. The oligosilicate exhibits a similar behaviour to the cyclosilicate. However, the Na charge distribution of the oligostructure is slightly broader than that of the K case, as observed in the results obtained using the optimized The Ca charge distribution is very similar for all investigated models. The main difference between the cyclo- and oligosilicate lies in the patterns of the O and Si charge distributions. The Si charge distribution in the cyclosilicate model displays three distinct peaks in the range of 0.4 e to 0.5 e. In contrast, the oligostructure only shows two peaks, which are slightly shifted to lower values, and the peak near 0.35 e is absent. The charge distribution of the O atoms follows a similar trend. The cyclosilicate exhibits several individual peaks in the range of −0.6 to −0.3 e. For the oligosilicate, the peak near −0.35 e is not present, and the remaining contributions are again shifted to smaller values. These differences are evident in both the experimental and the geometry-optimized structures.
![[Figure 9]](dk5130fig9thm.gif) | Figure 9 Comparison of the element-wise charge distributions based on the experimental (a) and optimized (b) structures, as well as the different elemental occupations of Na and K in the oligo- and the cyclosilicate. The distribution is represented by histograms obtained through kernel density estimation. |
Fig. 10(a) displays the associated molecular electronegativities of the experimental and geometry-optimized structures for the cyclo- and oligosilicate, respectively, considering full Na and K occupation, respectively. The values reveal a significant difference between the oligo- and the cyclosilicate, indicating the latter as the more stable structure (see also the results for the silica polymorphs shown in Fig. S3). Furthermore, there are small differences between the geometry of the optimized and experimental structures, which are more pronounced for the oligosilicate. Additionally, the K occupation for both silicate types leads to slightly higher values, indicating improved stability properties.
![[Figure 10]](dk5130fig10thm.gif) | Figure 10 (a) Comparison of the molecular electronegativities between the oligosilicate and the cyclosilicate with full Na and K occupancies using optimized and non-optimized idealized experimental structures. (b) Element density (numbers of elements per nm3) versus molecular between the geometry-optimized cyclo- and oligosilicate with Na/K occupation. |
Fig. 10(b) illustrates the element density versus the molecular plot, highlighting the varying impact of the ions on the molecular electronegativities. The data indicates that the difference in the oxygen density O per nm3 between the cyclo- and the oligosilicate is around 30 elements per nm3, while the other elements show considerably smaller differences of at most 10 elements per nm3. This suggests that the variation in molecular can be largely explained by differences in charge transfer involving the oxygen atoms. Only slight differences in element densities are observed between the Na- and K-occupied models for the cyclosilicate. These differences can be directly correlated with the different cell volumes of the optimized structures.
4. Discussion
Unbranched oligoanions [SimO3m+1]−(2m+2) based on the condensation of a finite number m of [SiO4] tetrahedra are rare among natural and synthetic silicates. Although structures containing [Si2O7] groups (m = 2) are still common, the number of representatives for the cases with m > 2 appears to decrease with increasing m (Liebau, 1985). Wierzbicka-Wieczorek et al. (2010a,b) provide a comparatively recent summary of oligosilicates with m = 3 and m = 4. Only one compound each has been identified so far for m = 5, 8, 9 and 10: Na4Sn2[Si5O16]·H2O (Safronov et al., 1983); Mg15.61Sc1.37(Mg0.30Si0.02)[Si8O25]2; Mg17.40Sc1.49(Mg0.15Si0.11)[Si9O28]2; Mg19.60Sc1.28(Mg0.04Si0.22)[Si10O31]2 (Takéuchi et al., 1984). Pb7[Si6O19] was found to be composed of heptameric [Si7O22] and tetrameric [Si4O13] units in a 2:1 ratio (Siidra et al., 2014).
Medaite (Mn2+6[V5+Si5O18(OH)]; Gramaccioli et al., 1981) is also of interest due to the [VSi5O18(OH)]12− oligoanion, which contains five [SiO4] or [SiO3(OH)] groups and an additional terminal [VO4] tetrahedron. Depending on the strictness of the silicate classification, medaite could be assigned either to the class with m = 6 (if tetrahedrally coordinated cations other than Si are considered) or to the class with m = 5 (if only SiO4 units are counted).
To the best of our knowledge, the present compound represents the first silicate in which [Si6O19] anions have been identified. There are no apparent structural similarities between medaite and the K–Na–Ca silicate described in this paper. Furthermore, the conformation of the oligoanions is quite different. In contrast to the highly corrugated arrangement of the hexamers in K0.72Na1.71Ca5.79Si6O19, the six tetrahedra in the corresponding cluster observed in medaite show an almost linear sequence. As phosphates and silicates frequently share similar features in their crystal chemistry (Averbuch-Pouchot & Durif, 1996), it was obvious to search also for crystalline compounds based on [P6O19] clusters. Only one representative has been reported so far: Ca4[P6O19] (Höppe, 2005). The [P6O19] groups have a strongly folded geometry, but the three different P—P—P—P torsion angles within the group are either almost 180° or 0°. This means that the folding of the hexamer is restricted to the plane defined by the six phosphorus atoms and does not have any out-of-plane component.
A few aluminates and gallates containing folded [Al6O19] and [Ga6O19] units that are more closely related to the present silicate have been reported in the literature. These include Sr10Al6O19 (Kahlenberg, 2002a), isostructural α-Sr10Ga6O19 (Kahlenberg, 2001; Krüger et al., 2009) and β-Sr10Ga6O19 (Kahlenberg, 2002b). In all three cases, the three torsion angles T—T—T—T (T: Si, Al and Ga) are approximately +90° (`+') or −90° (`−'). The conformation of the hexamer in K0.72Na1.71Ca5.79Si6O19 is (+, −, +) and also occurs in the β-Sr10Ga6O19. However, due to the centrosymmetry of the of the oxogallate, 50% of the [Ga6O19] groups display the inverted conformation (−, +, −). In centrosymmetric Sr10Al6O19 and α-Sr10Ga6O19 different pairs of conformations are realized: (+, −, −) and (−, +, +), respectively.
The similarity between K0.72Na1.71Ca5.79Si6O19 and β-Sr10Ga6O19 extends beyond the conformation of the oligomers. Similar to the silicate phase, the [Ga6O19] units also centre pseudo-cubic modules defined by the non-tetrahedrally coordinated cations (Kahlenberg, 2002b). There is a slight difference between the distorted cube in β-Sr10Ga6O19 and the oligosilicate. This difference is due to additional strontium ions occupying the very centre of each distorted cube in the β-phase, whereas the corresponding position in the oligosilicate is empty.
Joining the two open ends of the oligomer in K0.72Na1.71Ca5.79Si6O19 results in the formation of a closed highly puckered [Si6O18] ring located in the centre of the aforementioned pseudo-cubic module. This specific structural feature is actually realized in a large number of inorganic compounds belonging to the so-called lovozerite-type of structures (Pekov et al., 2009). Combeite, which is ideally Na4Ca4[Si6O18] is a chemically related member of this group (Fischer & Tillmanns, 1987). Fig. 3(c) illustrates the corresponding basic module, highlighting its similarity to the present compound.
The computational results indicate that the vibrational spectrum of the measured system can be adequately represented by the idealized fully K-occupied oligosilicate structure. The observed differences in intensity can be explained by the idealized occupation of partially occupied sites, as well as by the 0 K conditions associated with the use of energy-minimized structures. During the measurements, other effects such as luminescence may occur, which could cause slight deviations between the experimental and calculated spectra. The comparison of the molecular electronegativities of the Na- and K-saturated oligo- and cyclosilicates were compared, and it was found that the latter corresponds to the more stable structure. The oligosilicate exhibits lower stability due to its distinct charge transfer properties in the EEM calculation, which can be directly attributed to the oxygen atoms of the open [Si6O19] moieties. This is particularly evident in the molecular difference considering the number of elements per nm3, where the oxygen atoms have the greatest impact on the calculation results. The EEM data indicate that the energy-minimized geometries in this case do not significantly differ from those of the experimental structures using idealized occupancies. Therefore, the outlined EEM implementation offers an efficient framework for analysing the stability of various systems. This study shows that the EEM approach, which is simple and cost-effective, can be extended to the characterization of the quaternary system K2O–Na2O–CaO–SiO2 without pre-optimization of the experimentally determined geometry. The initial assessments can also aid in the preselection of analyses and systems without excessive effort. In the future, our EEM approach could be a used as part of analytical techniques to better understand quaternary systems such as K2O–Na2O–CaO–SiO2.
5. Conclusion
Liebau (1985) used Pauling's rule of parsimony to explain the decreasing stability of [SimO3m+1] units with increasing m in his seminal book on the crystal chemistry of silicates. The rule states that a crystalline compound tends to have the smallest possible number of different constituents or building elements. As the number of chemically non-equivalent [SiO4] tetrahedra increases with increasing m, a [Si5O16] unit (m = 5) should be less stable than a [Si2O7] dimer (m = 2). It is noteworthy that Liebau (1985) correlated the (relative) stability of oligomers having a specific value of m with the number of the corresponding observed crystal structures. This hypothesis is actually supported when comparing the number of published crystal structures with m = 5 and m = 2, respectively. Further research could involve EEM calculations to compare the molecular electronegativities of oligomers with different values of m. Furthermore, such study could also verify or falsify the existence of a minimum stability point at m = 7, as suggested by Liebau (1985). According to Liebau's argument, stability is positively correlated with the number of representatives, implying that [Si6O18] rings should be more stable than [Si6O19] groups. Our investigation has quantified this assumption using two specific examples.
The new oligosilicate structure type was determined from a single-crystal with a particular chemical composition. However, numerous examples from the mineral kingdom and from synthetic silicates demonstrate extensive cation substitutions between Na and K, and Na and Ca, respectively. It is therefore more than likely that the compound under investigation belongs to a more complex solid-solution series. A detailed analysis of the compositional space of these mixed crystals was not within the scope of this study. Further research could be conducted to examine the growth of single crystals at the compositions of the hypothetical solid-solution series, in conjunction with structural investigations. This could prove a fruitful study, shedding more light on the compound's structural response to the replacement of the alkali and alkaline-earth cations.
In particular, the EEM calculations have demonstrated that the newly synthesized oligosilicate is notably less stable than its cyclosilicate counterpart, regardless of whether Na+ or K+ are present as counterions. The new shielded EEM approach showed that it is a fast and computational cost-effective method for identifying relative stability differences in silicates. Consequently, this approach has the potential to be extended to other silicate systems in the future.
APPENDIX A
equalization method – theoretical overview
(χ) is a chemical property that describes the tendency of charge transfer phenomena between individual atoms. Its counterpart, chemical hardness (η), measures an atom's ability to resist provides an estimation of the bond formation potential, which is directly related to the structural stability in the ground state (Shankar & Parr, 1985). Both parameters can be very powerful quantities, providing initial insights into the properties of solid-state structures at low computational cost. It is important to note that these properties can be derived directly from DFT (Argaman & Makov, 2000; Brink, 2002; Jones, 2015; Yu et al., 2016).
The relationship between electron density ρ and χ can be described by the change in ground state energy E, as shown in the following equation (1)
![[{\rm d}E[\rho] = \,\mu {\rm d}N + \smallint \rho(r){\rm d}V(r){\rm d}r. \eqno(1)]](teximages/dk5130fd1.svg){kind=small}
Here, V(r) represents the external potential, N is the number of electrons and μ is the According to Shankar & Parr (1985), the is the negative value of in equation (2)
![[\chi = - \mu. \eqno (2)]](teximages/dk5130fd2.svg){kind=small}
The EEM, formulated by Mortier et al. (1985, 1986) is an efficient framework for computing and charge distributions. The basic following formalism is given by equation (3)
![[\chi_{\rm mol} = \chi_{i}^{0} + 2 \eta_{i}^{0} \,q_i + {{1}\over{4\pi \varepsilon_{0}}} \textstyle \sum \limits_{i \neq j}^{N} {{q_{j}}\over{r_{ij}}}, \eqno (3)]](teximages/dk5130fd3.svg){kind=small}
where χmol represents the molecular ![[\chi _i^0]](teximages/dk5130fi2.svg){kind=small}
and ![[\eta _i^0]](teximages/dk5130fi3.svg){kind=small}
are the atomic and hardness parameters of the ith atom, and qi represents the respective atomic partial charge. To describe the electrostatic interactions for a solid-state system, periodic boundary conditions must be considered, which may be included, for example, by a Madelung contribution (Jones & Templeton, 1956) obtained via the Ewald summation (Ewald, 1921; Stenberg & Stenqvist, 2020). The Coulomb interaction is divided into a short-range contribution carried out in and a long-range contribution in real space. To accelerate the approach, the interaction is simplified by using a Wolf summation (Wolf et al., 1999) which is well justified via local neutrality. The EEM equations in this formalism are modified by the inclusion of a damping parameter κ and take the form of equation (4):
![[\chi_{\rm mol} = \chi_{i}^{0} + 2 \eta_{i}^{0}\, q_i + {{1}\over{4\pi \varepsilon_{0}}} \left ( {\textstyle \sum \limits_{i \neq j}^{N}}{{q_{j}\,{\rm erfc}(\kappa r_{ij})}\over{r_{ij}}} - {{q_{j}\,{\rm erfc}(\kappa r_{\rm cut})}\over{r_{\rm cut}}} \right), \eqno (4)]](teximages/dk5130fd4.svg){kind=small}
where rcut is a suitable cut-off radius that is set to half of the smallest unit-cell parameter. In recent years, various studies (Demontis et al., 2001; Zahn et al., 2002; Fennell & Gezelter, 2006; Chen et al., 2010; Gdoutos et al., 2010; Kannam et al., 2012; Viveros-Méndez & Gil-Villegas, 2012; Fukuda & Nakamura, 2012) have successfully tested this simplified approach. However, finding suitable atomic parameters and remains a particular challenge for the EEM approach, especially in non-binary systems like the quaternary system K2O–Na2O–CaO–SiO2.
The ReaxFF reactive force field approach (Senftle et al., 2016; Leven et al., 2021) is a especially successful modelling technique for solid-state systems. It is based on charge equilibration schemes, such as the EEM method, and includes a shielding factor γ (Van Duin, 2009) to dampen overly strong short-range interactions. Parameter sets for χ0, η0 and γ can be found in the literature for most elements, which have proven adequate for the EEM approach used in this work.
The EEM framework can then be described by equation (5)
![[\chi_{\rm mol} = \chi_{i}^{0} + 2 \eta_{i}^{0}q_i + {{1}\over{4\pi \varepsilon_{0}}} \left ( {\textstyle \sum \limits_{i \neq j}^{N}} {{q_{j}{\rm erfc}(\kappa r_{ij})}\over{(r_{ij}^{3} + \gamma_{ij}^{-3})^{1/3}}}\right), \eqno (5)]](teximages/dk5130fd5.svg){kind=small}
where γij = (γi γj)1/2 is the geometric mean of the atomic damping parameters taken from the ReaxFF parameterization by Joshi et al. (2014).
APPENDIX B
Validation of the shielded equalization method approach
The EEM approach was validated by comparing the stabilization energies determined for a test set of four different small silica structures containing α-cristobalite (Dera et al., 2011), α-quartz (Antao et al., 2008), coesite (Angel et al., 2003) and stishovite (Hill et al., 1983) with unit-cell parameters < 15 Å against reference data taken from the literature (Van Genechten et al., 1987; Van Genechten & Mortier, 1988; Verstraelen et al., 2012) (see also Fig. S1). The initial geometries of the aforementioned crystal structures were optimized at DFT level using the Crystal23 program (Erba et al., 2023) before conducting the EEM calculations. The HSEsol functional (Schimka et al., 2011), which is a reliable option for treating solid-state systems, was used in combination with the pob-DZVP-rev2 and pob-TZVP-rev2 basis sets (Vilela Oliveira et al., 2019). A shrinking factor of 4 was used for (BZ) sampling, and the convergence criterion for energy was set to 10−8 Hartree, which proved to be sufficient. The optimized unit-cell parameters are available in supporting information Table S1 and in Table S2 a comparison between the unoptimized and optimized unit-cell parameters can be found.
The EEM calculations were performed using an in-house developed EEM algorithm capable of treating periodic systems. The EEM framework from equation (5) was applied to the geometry optimized structures. The relevant ReaxFF parameters, taken from Joshi et al. (2014), are listed in Table 5. The molecular electronegativities of the results were compared to literature values (Van Genechten et al., 1987; Henry, 1997), while also assessing the impact of the basis sets applied in the DFT structure optimization.
Supporting information
CCDC reference: 2372966
contains datablocks global, I. DOI: https://doi.org/10.1107/S2052520624007352/dk5130sup1.cif
Structure factors: contains datablock I. DOI: https://doi.org/10.1107/S2052520624007352/dk5130Isup2.hkl
Supplementary Tables and Figures. DOI: https://doi.org/10.1107/S2052520624007352/dk5130sup3.pdf
| Ca5.79K0.72Na1.71O19Si6 | Dx = 2.932 Mg m−3 |
| Mr = 771.93 | Mo Kα radiation, λ = 0.71073 Å |
| Tetragonal, P4122 | Cell parameters from 5866 reflections |
| a = 7.3659 (2) Å | θ = 4.2–30.3° |
| c = 32.2318 (18) Å | µ = 2.49 mm−1 |
| V = 1748.78 (12) Å3 | T = 296 K |
| Z = 4 | Prismatic fragment, colourless |
| F(000) = 1537 | 0.15 × 0.09 × 0.09 mm |
| Xcalibur, Ruby, Gemini ultra diffractometer | 1788 independent reflections |
| Radiation source: fine-focus sealed X-ray tube, Enhance (Mo) X-ray Source | 1690 reflections with I > 2σ(I) |
| Graphite monochromator | Rint = 0.055 |
| Detector resolution: 10.3575 pixels mm-1 | θmax = 26.4°, θmin = 2.8° |
| ω scans | h = −9→9 |
| Absorption correction: analytical CrysAlisPro 1.171.40.84a (Rigaku Oxford Diffraction, 2020) Analytical numeric absorption correction using a multifaceted crystal model based on expressions derived by R.C. Clark & J.S. Reid. (Clark, R. C. & Reid, J. S. (1995). Acta Cryst. A51, 887-897) | k = −9→9 |
| Tmin = 0.767, Tmax = 0.84 | l = −40→40 |
| 27647 measured reflections |
| Refinement on F2 | Secondary atom site location: difference Fourier map |
| Least-squares matrix: full | w = 1/[σ2(Fo2) + (0.0194P)2 + 2.3319P] where P = (Fo2 + 2Fc2)/3 |
| R[F2 > 2σ(F2)] = 0.024 | (Δ/σ)max = 0.001 |
| wR(F2) = 0.059 | Δρmax = 0.26 e Å−3 |
| S = 1.11 | Δρmin = −0.28 e Å−3 |
| 1788 reflections | Extinction correction: SHELXL, Fc*=kFc[1+0.001xFc2λ3/sin(2θ)]-1/4 |
| 164 parameters | Extinction coefficient: 0.00097 (9) |
| 0 restraints | Absolute structure: Flack H D (1983), Acta Cryst. A39, 876-881 |
| Primary atom site location: structure-invariant direct methods | Absolute structure parameter: −0.03 (5) |
Geometry. All s.u.'s (except the s.u. in the dihedral angle between two l.s. planes) are estimated using the full covariance matrix. The cell s.u.'s are taken into account individually in the estimation of s.u.'s in distances, angles and torsion angles; correlations between s.u.'s in cell parameters are only used when they are defined by crystal symmetry. An approximate (isotropic) treatment of cell s.u.'s is used for estimating s.u.'s involving l.s. planes. |
Refinement. Refinement of F2 against ALL reflections. The weighted R-factor wR and goodness of fit S are based on F2, conventional R-factors R are based on F, with F set to zero for negative F2. The threshold expression of F2 > 2σ(F2) is used only for calculating R-factors(gt) etc. and is not relevant to the choice of reflections for refinement. R-factors based on F2 are statistically about twice as large as those based on F, and R- factors based on ALL data will be even larger. |
| x | y | z | Uiso*/Ueq | Occ. (<1) | |
| Ca1 | 0.26555 (8) | 0.75140 (8) | 0.935179 (16) | 0.0098 (2) | 0.960 (8) |
| Na1 | 0.26555 (8) | 0.75140 (8) | 0.935179 (16) | 0.0098 (2) | 0.040 (8) |
| Ca2 | 0.01465 (8) | 0.01465 (8) | 0.875 | 0.0086 (3) | 0.964 (10) |
| Na2 | 0.01465 (8) | 0.01465 (8) | 0.875 | 0.0086 (3) | 0.036 (10) |
| Ca3 | 0 | 0.00304 (13) | 0 | 0.0103 (3) | 0.939 (10) |
| Na3 | 0 | 0.00304 (13) | 0 | 0.0103 (3) | 0.061 (10) |
| Ca4 | 0 | 0.46370 (12) | 0 | 0.0105 (3) | 0.959 (11) |
| Na4 | 0 | 0.46370 (12) | 0 | 0.0105 (3) | 0.041 (11) |
| Ca5 | 0.98400 (14) | 0.54019 (13) | 0.87809 (3) | 0.0145 (4) | 0.252 (7) |
| Na5 | 0.98400 (14) | 0.54019 (13) | 0.87809 (3) | 0.0145 (4) | 0.748 (7) |
| K6 | 0.5 | 0.03751 (15) | 0 | 0.0174 (2) | 0.5 |
| Ca6 | 0.5 | 0.03751 (15) | 0 | 0.0174 (2) | 0.5 |
| K7 | 0.5 | 0.5004 (7) | 0 | 0.0198 (16) | 0.217 (4) |
| Si1 | 0.28110 (11) | 0.26520 (10) | 0.92558 (2) | 0.00752 (18) | |
| Si2 | 0.71619 (11) | 0.30209 (11) | 0.93169 (2) | 0.00855 (19) | |
| Si3 | 0.75279 (11) | 0.73591 (10) | 0.94637 (2) | 0.00791 (18) | |
| O1 | 0.1835 (3) | 0.4472 (3) | 0.94025 (7) | 0.0181 (5) | |
| O2 | 0.9324 (3) | 0.8070 (3) | 0.92317 (6) | 0.0148 (5) | |
| O3 | 0.7907 (3) | 0.7488 (3) | 0.99576 (6) | 0.0178 (5) | |
| O4 | 0.8108 (3) | 0.2182 (3) | 0.97169 (6) | 0.0167 (5) | |
| O5 | 0.7869 (3) | 0.2338 (3) | 0.88731 (6) | 0.0200 (5) | |
| O6 | 0.5644 (3) | 0.8268 (4) | 0.93354 (7) | 0.0239 (6) | |
| O7 | 0.2032 (3) | 0.0745 (3) | 0.94075 (6) | 0.0121 (5) | |
| O8 | 0.4975 (3) | 0.2672 (3) | 0.93523 (8) | 0.0259 (6) | |
| O9 | 0.2562 (3) | 0.2562 (3) | 0.875 | 0.0294 (9) | |
| O10 | 0.7512 (4) | 0.5192 (3) | 0.93384 (7) | 0.0275 (6) |
| U11 | U22 | U33 | U12 | U13 | U23 | |
| Ca1 | 0.0111 (4) | 0.0096 (4) | 0.0085 (3) | −0.0010 (3) | 0.0013 (2) | 0.0003 (2) |
| Na1 | 0.0111 (4) | 0.0096 (4) | 0.0085 (3) | −0.0010 (3) | 0.0013 (2) | 0.0003 (2) |
| Ca2 | 0.0080 (4) | 0.0080 (4) | 0.0096 (4) | −0.0009 (3) | −0.0014 (2) | 0.0014 (2) |
| Na2 | 0.0080 (4) | 0.0080 (4) | 0.0096 (4) | −0.0009 (3) | −0.0014 (2) | 0.0014 (2) |
| Ca3 | 0.0074 (5) | 0.0076 (5) | 0.0159 (5) | 0 | 0.0012 (4) | 0 |
| Na3 | 0.0074 (5) | 0.0076 (5) | 0.0159 (5) | 0 | 0.0012 (4) | 0 |
| Ca4 | 0.0107 (5) | 0.0106 (6) | 0.0101 (5) | 0 | 0.0028 (4) | 0 |
| Na4 | 0.0107 (5) | 0.0106 (6) | 0.0101 (5) | 0 | 0.0028 (4) | 0 |
| Ca5 | 0.0160 (6) | 0.0155 (6) | 0.0119 (5) | −0.0020 (4) | −0.0007 (4) | −0.0022 (4) |
| Na5 | 0.0160 (6) | 0.0155 (6) | 0.0119 (5) | −0.0020 (4) | −0.0007 (4) | −0.0022 (4) |
| K6 | 0.0214 (5) | 0.0186 (6) | 0.0121 (4) | 0 | 0.0020 (4) | 0 |
| Ca6 | 0.0214 (5) | 0.0186 (6) | 0.0121 (4) | 0 | 0.0020 (4) | 0 |
| K7 | 0.018 (3) | 0.025 (3) | 0.017 (2) | 0 | 0.0053 (19) | 0 |
| Si1 | 0.0073 (4) | 0.0079 (4) | 0.0074 (3) | −0.0011 (3) | −0.0002 (3) | −0.0005 (3) |
| Si2 | 0.0085 (4) | 0.0079 (4) | 0.0093 (3) | −0.0008 (3) | −0.0004 (3) | −0.0012 (3) |
| Si3 | 0.0079 (4) | 0.0073 (4) | 0.0085 (3) | −0.0005 (3) | −0.0006 (3) | 0.0001 (3) |
| O1 | 0.0233 (13) | 0.0092 (11) | 0.0219 (11) | 0.0003 (10) | 0.0076 (10) | 0.0009 (9) |
| O2 | 0.0123 (11) | 0.0152 (12) | 0.0167 (10) | −0.0005 (9) | 0.0018 (9) | 0.0041 (10) |
| O3 | 0.0187 (12) | 0.0236 (12) | 0.0111 (10) | −0.0063 (10) | −0.0005 (8) | 0.0007 (9) |
| O4 | 0.0152 (11) | 0.0238 (13) | 0.0110 (10) | 0.0055 (10) | −0.0013 (8) | −0.0014 (9) |
| O5 | 0.0296 (13) | 0.0215 (12) | 0.0088 (9) | 0.0118 (11) | −0.0014 (9) | −0.0010 (8) |
| O6 | 0.0107 (12) | 0.0284 (15) | 0.0326 (13) | 0.0004 (10) | −0.0020 (10) | 0.0142 (12) |
| O7 | 0.0135 (11) | 0.0089 (10) | 0.0138 (10) | −0.0001 (9) | 0.0021 (9) | −0.0012 (8) |
| O8 | 0.0096 (11) | 0.0255 (14) | 0.0427 (14) | −0.0033 (12) | −0.0057 (10) | 0.0091 (11) |
| O9 | 0.0405 (14) | 0.0405 (14) | 0.0072 (13) | −0.0183 (19) | 0.0037 (11) | −0.0037 (11) |
| O10 | 0.0393 (17) | 0.0114 (12) | 0.0320 (13) | −0.0096 (13) | 0.0106 (12) | −0.0069 (10) |
| Ca1—O3i | 2.2643 (19) | K7—O10xiii | 2.827 (2) |
| Ca1—O6 | 2.271 (2) | K7—O1xiii | 3.049 (3) |
| Ca1—O1 | 2.326 (2) | K7—O1viii | 3.049 (3) |
| Ca1—O5ii | 2.3627 (19) | Si1—O1 | 1.593 (2) |
| Ca1—O7iii | 2.430 (2) | Si1—O7 | 1.594 (2) |
| Ca1—O2iv | 2.518 (2) | Si1—O8 | 1.624 (2) |
| Na1—O3i | 2.2643 (19) | Si1—O9 | 1.6420 (8) |
| Na1—O6 | 2.271 (2) | Si2—O4 | 1.590 (2) |
| Na1—O1 | 2.326 (2) | Si2—O5 | 1.603 (2) |
| Na1—O5ii | 2.3627 (19) | Si2—O10 | 1.621 (2) |
| Na1—O7iii | 2.430 (2) | Si2—O8 | 1.635 (2) |
| Na1—O2iv | 2.518 (2) | Si3—O6 | 1.595 (3) |
| Ca2—O2v | 2.262 (2) | Si3—O2 | 1.607 (2) |
| Ca2—O2vi | 2.262 (2) | Si3—O3 | 1.619 (2) |
| Ca2—O5vii | 2.362 (2) | Si3—O10 | 1.647 (2) |
| Ca2—O5iv | 2.362 (2) | O1—Si1 | 1.593 (2) |
| Ca2—O9 | 2.516 (3) | O1—Ca1 | 2.326 (2) |
| Ca2—O7 | 2.572 (2) | O1—Na1 | 2.326 (2) |
| Ca2—O7ii | 2.572 (2) | O1—Ca4xvii | 2.356 (2) |
| Na2—O2v | 2.262 (2) | O1—Na4xvii | 2.356 (2) |
| Na2—O2vi | 2.262 (2) | O1—Ca5iv | 2.577 (3) |
| Na2—O5vii | 2.362 (2) | O1—Na5iv | 2.577 (3) |
| Na2—O5iv | 2.362 (2) | O1—K7xvii | 3.049 (3) |
| Na2—O9 | 2.516 (3) | O2—Si3 | 1.607 (2) |
| Na2—O7 | 2.572 (2) | O2—Ca2xviii | 2.262 (2) |
| Na2—O7ii | 2.572 (2) | O2—Na2xviii | 2.262 (2) |
| Ca3—O4viii | 2.299 (2) | O2—Ca5 | 2.473 (2) |
| Ca3—O4ix | 2.299 (2) | O2—Na5 | 2.473 (2) |
| Ca3—O3x | 2.429 (2) | O2—Ca1xiv | 2.518 (2) |
| Ca3—O3xi | 2.429 (2) | O2—Na1xiv | 2.518 (2) |
| Ca3—O7xii | 2.483 (2) | O2—Ca3xix | 2.910 (2) |
| Ca3—O7xiii | 2.483 (2) | O2—Na3xix | 2.910 (2) |
| Ca3—O2x | 2.910 (2) | O3—Si3 | 1.619 (2) |
| Ca3—O2xi | 2.910 (2) | O3—Ca1i | 2.2643 (19) |
| Na3—O4viii | 2.299 (2) | O3—Na1i | 2.2643 (19) |
| Na3—O4ix | 2.299 (2) | O3—Ca3xix | 2.429 (2) |
| Na3—O3x | 2.429 (2) | O3—Na3xix | 2.429 (2) |
| Na3—O3xi | 2.429 (2) | O3—Ca4xx | 2.609 (2) |
| Na3—O7xii | 2.483 (2) | O3—Na4xx | 2.609 (2) |
| Na3—O7xiii | 2.483 (2) | O3—K7xvii | 2.820 (4) |
| Na3—O2x | 2.910 (2) | O3—Ca6xxi | 3.021 (2) |
| Na3—O2xi | 2.910 (2) | O3—K6xxi | 3.021 (2) |
| Ca4—O1xii | 2.356 (2) | O4—Si2 | 1.590 (2) |
| Ca4—O1xiii | 2.356 (2) | O4—Ca3xx | 2.299 (2) |
| Ca4—O4ix | 2.459 (2) | O4—Na3xx | 2.299 (2) |
| Ca4—O4viii | 2.459 (2) | O4—Ca4xx | 2.459 (2) |
| Ca4—O3viii | 2.609 (2) | O4—Na4xx | 2.459 (2) |
| Ca4—O3ix | 2.609 (2) | O4—Ca6xvii | 2.801 (2) |
| Ca4—O10viii | 2.841 (3) | O4—K6xvii | 2.801 (2) |
| Ca4—O10ix | 2.841 (3) | O4—K7xvii | 3.224 (4) |
| Na4—O1xii | 2.356 (2) | O5—Si2 | 1.603 (2) |
| Na4—O1xiii | 2.356 (2) | O5—Ca2xiv | 2.362 (2) |
| Na4—O4ix | 2.459 (2) | O5—Na2xiv | 2.362 (2) |
| Na4—O4viii | 2.459 (2) | O5—Ca1ii | 2.3627 (19) |
| Na4—O3viii | 2.609 (2) | O5—Na1ii | 2.3627 (19) |
| Na4—O3ix | 2.609 (2) | O5—Ca5vii | 2.634 (3) |
| Na4—O10viii | 2.841 (3) | O5—Na5vii | 2.634 (3) |
| Na4—O10ix | 2.841 (3) | O5—Ca5 | 2.700 (3) |
| Ca5—O6ii | 2.306 (2) | O5—Na5 | 2.700 (3) |
| Ca5—O2 | 2.473 (2) | O6—Si3 | 1.595 (3) |
| Ca5—O10 | 2.488 (3) | O6—Ca1 | 2.271 (2) |
| Ca5—O1xiv | 2.577 (3) | O6—Na1 | 2.271 (2) |
| Ca5—O5xv | 2.634 (3) | O6—Ca5ii | 2.306 (2) |
| Ca5—O5 | 2.700 (3) | O6—Na5ii | 2.306 (2) |
| Ca5—O9xiv | 2.8993 (10) | O6—Ca6xxi | 2.687 (3) |
| Ca5—O8xv | 2.935 (3) | O6—K6xxi | 2.687 (3) |
| Na5—O6ii | 2.306 (2) | O6—K7xvii | 3.255 (5) |
| Na5—O2 | 2.473 (2) | O7—Si1 | 1.594 (2) |
| Na5—O10 | 2.488 (3) | O7—Ca1xxii | 2.430 (2) |
| Na5—O1xiv | 2.577 (3) | O7—Na1xxii | 2.430 (2) |
| Na5—O5xv | 2.634 (3) | O7—Ca3xvii | 2.483 (2) |
| Na5—O5 | 2.700 (3) | O7—Na3xvii | 2.483 (2) |
| Na5—O9xiv | 2.8993 (10) | O7—Ca2 | 2.572 (2) |
| Na5—O8xv | 2.935 (3) | O7—Na2 | 2.572 (2) |
| Ca6—O8viii | 2.687 (2) | O7—Ca6xvii | 2.916 (2) |
| Ca6—O8xiii | 2.687 (2) | O7—K6xvii | 2.916 (2) |
| Ca6—O6xvi | 2.687 (3) | O8—Si1 | 1.624 (2) |
| Ca6—O6xi | 2.687 (3) | O8—Si2 | 1.635 (2) |
| Ca6—O4xiii | 2.801 (2) | O8—Ca6xvii | 2.687 (2) |
| Ca6—O4viii | 2.801 (2) | O8—K6xvii | 2.687 (2) |
| Ca6—O7viii | 2.916 (2) | O8—K7xvii | 2.703 (4) |
| Ca6—O7xiii | 2.916 (2) | O8—Ca5vii | 2.935 (3) |
| Ca6—O3xi | 3.021 (2) | O8—Na5vii | 2.935 (3) |
| Ca6—O3xvi | 3.021 (2) | O9—Si1 | 1.6420 (8) |
| K6—O8viii | 2.687 (2) | O9—Si1ii | 1.6420 (8) |
| K6—O8xiii | 2.687 (2) | O9—Ca2 | 2.516 (3) |
| K6—O6xvi | 2.687 (3) | O9—Na2 | 2.516 (3) |
| K6—O6xi | 2.687 (3) | O9—Ca5iv | 2.8993 (10) |
| K6—O4xiii | 2.801 (2) | O9—Na5iv | 2.8993 (10) |
| K6—O4viii | 2.801 (2) | O9—Ca5vii | 2.8993 (10) |
| K6—O7viii | 2.916 (2) | O9—Na5vii | 2.8993 (10) |
| K6—O7xiii | 2.916 (2) | O10—Si2 | 1.621 (2) |
| K6—O3xi | 3.021 (2) | O10—Si3 | 1.647 (2) |
| K6—O3xvi | 3.021 (2) | O10—Ca5 | 2.488 (3) |
| K7—O8xiii | 2.703 (4) | O10—Na5 | 2.488 (3) |
| K7—O8viii | 2.703 (4) | O10—K7xvii | 2.827 (2) |
| K7—O3xiii | 2.820 (4) | O10—Ca4xx | 2.841 (3) |
| K7—O3viii | 2.820 (4) | O10—Na4xx | 2.841 (3) |
| K7—O10viii | 2.827 (2) | ||
| O3i—Ca1—O6 | 101.67 (9) | Ca1—O1—Ca5iv | 80.66 (7) |
| O3i—Ca1—O1 | 82.84 (8) | Na4xvii—O1—Ca5iv | 107.14 (10) |
| O6—Ca1—O1 | 119.28 (9) | Ca4xvii—O1—Ca5iv | 107.14 (10) |
| O3i—Ca1—O5ii | 162.75 (8) | Na5iv—O1—Ca5iv | 0.00 (5) |
| O6—Ca1—O5ii | 92.63 (8) | Si1—O1—K7xvii | 87.15 (13) |
| O1—Ca1—O5ii | 98.65 (8) | Ca1—O1—K7xvii | 73.86 (12) |
| O3i—Ca1—O7iii | 84.32 (7) | Na4xvii—O1—K7xvii | 85.16 (7) |
| O6—Ca1—O7iii | 86.87 (9) | Ca4xvii—O1—K7xvii | 85.16 (7) |
| O1—Ca1—O7iii | 152.72 (8) | Na5iv—O1—K7xvii | 153.23 (13) |
| O5ii—Ca1—O7iii | 86.90 (7) | Ca5iv—O1—K7xvii | 153.23 (13) |
| O3i—Ca1—O2iv | 88.52 (8) | Si3—O2—Na2xviii | 139.48 (13) |
| O6—Ca1—O2iv | 154.35 (8) | Si3—O2—Ca2xviii | 139.48 (13) |
| O1—Ca1—O2iv | 85.07 (8) | Na2xviii—O2—Ca2xviii | 0 |
| O5ii—Ca1—O2iv | 74.55 (7) | Si3—O2—Ca5 | 98.12 (11) |
| O7iii—Ca1—O2iv | 70.61 (8) | Na2xviii—O2—Ca5 | 95.33 (8) |
| O2v—Ca2—O2vi | 96.23 (12) | Ca2xviii—O2—Ca5 | 95.33 (8) |
| O2v—Ca2—O5vii | 99.01 (8) | Si3—O2—Ca1xiv | 132.66 (11) |
| O2vi—Ca2—O5vii | 79.52 (8) | Na2xviii—O2—Ca1xiv | 87.38 (7) |
| O2v—Ca2—O5iv | 79.52 (8) | Ca2xviii—O2—Ca1xiv | 87.38 (7) |
| O2vi—Ca2—O5iv | 99.01 (8) | Ca5—O2—Ca1xiv | 79.12 (7) |
| O5vii—Ca2—O5iv | 177.84 (13) | Si3—O2—Na1xiv | 132.66 (11) |
| O2v—Ca2—O9 | 131.88 (6) | Na2xviii—O2—Na1xiv | 87.38 (7) |
| O2vi—Ca2—O9 | 131.88 (6) | Ca2xviii—O2—Na1xiv | 87.38 (7) |
| O5vii—Ca2—O9 | 91.08 (7) | Ca5—O2—Na1xiv | 79.12 (7) |
| O5iv—Ca2—O9 | 91.08 (7) | Ca1xiv—O2—Na1xiv | 0.00 (4) |
| O2v—Ca2—O7 | 167.57 (8) | Si3—O2—Na3xix | 84.63 (9) |
| O2vi—Ca2—O7 | 72.25 (7) | Na2xviii—O2—Na3xix | 101.69 (8) |
| O5vii—Ca2—O7 | 83.74 (7) | Ca2xviii—O2—Na3xix | 101.69 (8) |
| O5iv—Ca2—O7 | 97.36 (7) | Ca5—O2—Na3xix | 150.22 (9) |
| O9—Ca2—O7 | 59.80 (5) | Ca1xiv—O2—Na3xix | 77.46 (6) |
| O2v—Ca2—O7ii | 72.25 (7) | Na1xiv—O2—Na3xix | 77.46 (6) |
| O2vi—Ca2—O7ii | 167.57 (8) | Si3—O2—Ca3xix | 84.63 (9) |
| O5vii—Ca2—O7ii | 97.36 (7) | Na2xviii—O2—Ca3xix | 101.69 (8) |
| O5iv—Ca2—O7ii | 83.74 (7) | Ca2xviii—O2—Ca3xix | 101.69 (8) |
| O9—Ca2—O7ii | 59.80 (5) | Ca5—O2—Ca3xix | 150.22 (9) |
| O7—Ca2—O7ii | 119.60 (11) | Ca1xiv—O2—Ca3xix | 77.46 (6) |
| O4viii—Ca3—O4ix | 92.87 (12) | Na1xiv—O2—Ca3xix | 77.46 (6) |
| O4viii—Ca3—O3x | 159.76 (7) | Na3xix—O2—Ca3xix | 0 |
| O4ix—Ca3—O3x | 97.13 (8) | Si3—O3—Na1i | 159.32 (14) |
| O4viii—Ca3—O3xi | 97.13 (8) | Si3—O3—Ca1i | 159.32 (14) |
| O4ix—Ca3—O3xi | 159.76 (7) | Na1i—O3—Ca1i | 0.00 (3) |
| O3x—Ca3—O3xi | 79.15 (11) | Si3—O3—Na3xix | 102.13 (10) |
| O4viii—Ca3—O7xii | 85.07 (7) | Na1i—O3—Na3xix | 93.11 (7) |
| O4ix—Ca3—O7xii | 78.10 (7) | Ca1i—O3—Na3xix | 93.11 (7) |
| O3x—Ca3—O7xii | 79.87 (7) | Si3—O3—Ca3xix | 102.13 (10) |
| O3xi—Ca3—O7xii | 120.17 (7) | Na1i—O3—Ca3xix | 93.11 (7) |
| O4viii—Ca3—O7xiii | 78.10 (7) | Ca1i—O3—Ca3xix | 93.11 (7) |
| O4ix—Ca3—O7xiii | 85.07 (7) | Na3xix—O3—Ca3xix | 0.00 (3) |
| O3x—Ca3—O7xiii | 120.17 (7) | Si3—O3—Na4xx | 96.09 (10) |
| O3xi—Ca3—O7xiii | 79.87 (7) | Na1i—O3—Na4xx | 93.63 (7) |
| O7xii—Ca3—O7xiii | 155.53 (11) | Ca1i—O3—Na4xx | 93.63 (7) |
| O4viii—Ca3—O2x | 141.60 (7) | Na3xix—O3—Na4xx | 104.04 (8) |
| O4ix—Ca3—O2x | 84.29 (7) | Ca3xix—O3—Na4xx | 104.04 (8) |
| O3x—Ca3—O2x | 57.38 (6) | Si3—O3—Ca4xx | 96.09 (10) |
| O3xi—Ca3—O2x | 76.94 (7) | Na1i—O3—Ca4xx | 93.63 (7) |
| O7xii—Ca3—O2x | 131.04 (7) | Ca1i—O3—Ca4xx | 93.63 (7) |
| O7xiii—Ca3—O2x | 63.50 (7) | Na3xix—O3—Ca4xx | 104.04 (8) |
| O4viii—Ca3—O2xi | 84.29 (7) | Ca3xix—O3—Ca4xx | 104.04 (8) |
| O4ix—Ca3—O2xi | 141.60 (7) | Na4xx—O3—Ca4xx | 0.00 (2) |
| O3x—Ca3—O2xi | 76.94 (7) | Si3—O3—K7xvii | 83.03 (9) |
| O3xi—Ca3—O2xi | 57.38 (6) | Na1i—O3—K7xvii | 79.56 (7) |
| O7xii—Ca3—O2xi | 63.50 (7) | Ca1i—O3—K7xvii | 79.56 (7) |
| O7xiii—Ca3—O2xi | 131.04 (7) | Na3xix—O3—K7xvii | 168.33 (12) |
| O2x—Ca3—O2xi | 120.49 (9) | Ca3xix—O3—K7xvii | 168.33 (12) |
| O4viii—Ca3—Si3x | 170.49 (5) | Na4xx—O3—K7xvii | 85.63 (10) |
| O1xii—Ca4—O1xiii | 174.09 (12) | Ca4xx—O3—K7xvii | 85.63 (10) |
| O1xii—Ca4—O4ix | 86.58 (8) | Si3—O3—K6xxi | 87.91 (9) |
| O1xiii—Ca4—O4ix | 89.08 (8) | Na1i—O3—K6xxi | 79.62 (6) |
| O1xii—Ca4—O4viii | 89.08 (8) | Ca1i—O3—K6xxi | 79.62 (6) |
| O1xiii—Ca4—O4viii | 86.58 (8) | Na3xix—O3—K6xxi | 84.53 (6) |
| O4ix—Ca4—O4viii | 85.30 (10) | Ca3xix—O3—K6xxi | 84.53 (6) |
| O1xii—Ca4—O3viii | 109.73 (8) | Na4xx—O3—K6xxi | 169.47 (9) |
| O1xiii—Ca4—O3viii | 75.25 (7) | Ca4xx—O3—K6xxi | 169.47 (9) |
| O4ix—Ca4—O3viii | 161.18 (6) | K7xvii—O3—K6xxi | 85.20 (11) |
| O4viii—Ca4—O3viii | 103.75 (7) | Si2—O4—Na3xx | 148.77 (12) |
| O1xii—Ca4—O3ix | 75.25 (7) | Si2—O4—Ca3xx | 148.77 (12) |
| O1xiii—Ca4—O3ix | 109.73 (8) | Na3xx—O4—Ca3xx | 0.00 (3) |
| O4ix—Ca4—O3ix | 103.75 (7) | Si2—O4—Na4xx | 105.26 (12) |
| O4viii—Ca4—O3ix | 161.18 (6) | Na3xx—O4—Na4xx | 90.91 (7) |
| O3viii—Ca4—O3ix | 72.78 (10) | Ca3xx—O4—Na4xx | 90.91 (7) |
| O1xii—Ca4—O10viii | 76.34 (8) | Si2—O4—Ca4xx | 105.26 (12) |
| O1xiii—Ca4—O10viii | 104.54 (8) | Na3xx—O4—Ca4xx | 90.91 (7) |
| O4ix—Ca4—O10viii | 138.59 (7) | Ca3xx—O4—Ca4xx | 90.91 (7) |
| O4viii—Ca4—O10viii | 57.43 (7) | Na4xx—O4—Ca4xx | 0.00 (3) |
| O3viii—Ca4—O10viii | 57.57 (6) | Si2—O4—K6xvii | 95.21 (10) |
| O3ix—Ca4—O10viii | 107.74 (7) | Na3xx—O4—K6xvii | 92.22 (8) |
| O1xii—Ca4—O10ix | 104.54 (8) | Ca3xx—O4—K6xvii | 92.22 (8) |
| O1xiii—Ca4—O10ix | 76.34 (8) | Na4xx—O4—K6xvii | 133.78 (8) |
| O4ix—Ca4—O10ix | 57.43 (7) | Ca4xx—O4—K6xvii | 133.78 (8) |
| O4viii—Ca4—O10ix | 138.59 (7) | Si2—O4—K7xvii | 70.60 (8) |
| O3viii—Ca4—O10ix | 107.74 (7) | Na3xx—O4—K7xvii | 139.68 (8) |
| O3ix—Ca4—O10ix | 57.57 (6) | Ca3xx—O4—K7xvii | 139.68 (8) |
| O10viii—Ca4—O10ix | 163.45 (10) | Na4xx—O4—K7xvii | 79.82 (8) |
| O6ii—Ca5—O2 | 111.55 (9) | Ca4xx—O4—K7xvii | 79.82 (8) |
| O6ii—Ca5—O10 | 106.32 (10) | K6xvii—O4—K7xvii | 68.52 (9) |
| O2—Ca5—O10 | 61.26 (8) | Si2—O5—Na2xiv | 126.52 (11) |
| O6ii—Ca5—O1xiv | 167.53 (10) | Si2—O5—Ca2xiv | 126.52 (11) |
| O2—Ca5—O1xiv | 80.92 (8) | Na2xiv—O5—Ca2xiv | 0.00 (2) |
| O10—Ca5—O1xiv | 79.34 (8) | Si2—O5—Na1ii | 144.63 (12) |
| O6ii—Ca5—O5xv | 97.76 (8) | Na2xiv—O5—Na1ii | 88.86 (7) |
| O2—Ca5—O5xv | 70.73 (7) | Ca2xiv—O5—Na1ii | 88.86 (7) |
| O10—Ca5—O5xv | 131.34 (8) | Si2—O5—Ca1ii | 144.63 (12) |
| O1xiv—Ca5—O5xv | 86.07 (8) | Na2xiv—O5—Ca1ii | 88.86 (7) |
| O6ii—Ca5—O5 | 83.66 (8) | Ca2xiv—O5—Ca1ii | 88.86 (7) |
| O2—Ca5—O5 | 121.12 (8) | Na1ii—O5—Ca1ii | 0.00 (3) |
| O10—Ca5—O5 | 59.87 (7) | Si2—O5—Na5vii | 99.39 (11) |
| O1xiv—Ca5—O5 | 89.94 (7) | Na2xiv—O5—Na5vii | 88.90 (8) |
| O5xv—Ca5—O5 | 166.74 (4) | Ca2xiv—O5—Na5vii | 88.90 (8) |
| O6ii—Ca5—O9xiv | 111.92 (8) | Na1ii—O5—Na5vii | 78.83 (7) |
| O2—Ca5—O9xiv | 134.42 (8) | Ca1ii—O5—Na5vii | 78.83 (7) |
| O10—Ca5—O9xiv | 117.16 (8) | Si2—O5—Ca5vii | 99.39 (11) |
| O1xiv—Ca5—O9xiv | 55.99 (6) | Na2xiv—O5—Ca5vii | 88.90 (8) |
| O5xv—Ca5—O9xiv | 90.47 (8) | Ca2xiv—O5—Ca5vii | 88.90 (8) |
| O5—Ca5—O9xiv | 76.85 (8) | Na1ii—O5—Ca5vii | 78.83 (7) |
| O6ii—Ca5—O8xv | 76.47 (9) | Ca1ii—O5—Ca5vii | 78.83 (7) |
| O2—Ca5—O8xv | 127.07 (8) | Na5vii—O5—Ca5vii | 0.00 (4) |
| O10—Ca5—O8xv | 170.10 (9) | Si2—O5—Ca5 | 90.62 (10) |
| O1xiv—Ca5—O8xv | 96.14 (8) | Na2xiv—O5—Ca5 | 99.84 (9) |
| O5xv—Ca5—O8xv | 56.37 (6) | Ca2xiv—O5—Ca5 | 99.84 (9) |
| O5—Ca5—O8xv | 111.67 (7) | Na1ii—O5—Ca5 | 82.42 (7) |
| O9xiv—Ca5—O8xv | 53.66 (6) | Ca1ii—O5—Ca5 | 82.42 (7) |
| O8viii—K6—O8xiii | 101.95 (12) | Na5vii—O5—Ca5 | 159.14 (8) |
| O8viii—K6—O6xvi | 169.00 (7) | Ca5vii—O5—Ca5 | 159.14 (8) |
| O8xiii—K6—O6xvi | 75.26 (8) | Si3—O6—Ca1 | 137.26 (15) |
| O8viii—K6—O6xi | 75.26 (8) | Si3—O6—Na5ii | 120.09 (13) |
| O8xiii—K6—O6xi | 169.00 (7) | Ca1—O6—Na5ii | 93.88 (9) |
| O6xvi—K6—O6xi | 109.45 (11) | Si3—O6—Ca5ii | 120.09 (13) |
| O8viii—K6—O4xiii | 87.05 (7) | Ca1—O6—Ca5ii | 93.88 (9) |
| O8xiii—K6—O4xiii | 56.85 (6) | Na5ii—O6—Ca5ii | 0.00 (5) |
| O6xvi—K6—O4xiii | 82.55 (7) | Si3—O6—K6xxi | 100.92 (11) |
| O6xi—K6—O4xiii | 132.72 (6) | Ca1—O6—K6xxi | 87.22 (8) |
| O8viii—K6—O4viii | 56.85 (6) | Na5ii—O6—K6xxi | 112.52 (11) |
| O8xiii—K6—O4viii | 87.05 (7) | Ca5ii—O6—K6xxi | 112.52 (11) |
| O6xvi—K6—O4viii | 132.72 (6) | Si3—O6—K7xvii | 69.28 (9) |
| O6xi—K6—O4viii | 82.55 (7) | Ca1—O6—K7xvii | 70.29 (6) |
| O4xiii—K6—O4viii | 123.26 (10) | Na5ii—O6—K7xvii | 157.88 (12) |
| O8viii—K6—O7viii | 55.06 (7) | Ca5ii—O6—K7xvii | 157.88 (12) |
| O8xiii—K6—O7viii | 117.08 (7) | K6xxi—O6—K7xvii | 82.90 (9) |
| O6xvi—K6—O7viii | 116.33 (7) | Si1—O7—Na1xxii | 140.55 (12) |
| O6xi—K6—O7viii | 70.38 (6) | Si1—O7—Ca1xxii | 140.55 (12) |
| O4xiii—K6—O7viii | 63.65 (6) | Na1xxii—O7—Ca1xxii | 0.00 (2) |
| O4viii—K6—O7viii | 110.80 (6) | Si1—O7—Na3xvii | 129.75 (11) |
| O8viii—K6—O7xiii | 117.08 (7) | Na1xxii—O7—Na3xvii | 87.89 (7) |
| O8xiii—K6—O7xiii | 55.06 (7) | Ca1xxii—O7—Na3xvii | 87.89 (7) |
| O6xvi—K6—O7xiii | 70.38 (6) | Si1—O7—Ca3xvii | 129.75 (11) |
| O6xi—K6—O7xiii | 116.33 (7) | Na1xxii—O7—Ca3xvii | 87.89 (7) |
| O4xiii—K6—O7xiii | 110.80 (6) | Ca1xxii—O7—Ca3xvii | 87.89 (7) |
| O4viii—K6—O7xiii | 63.65 (6) | Na3xvii—O7—Ca3xvii | 0.00 (4) |
| O7viii—K6—O7xiii | 169.29 (9) | Si1—O7—Ca2 | 95.32 (9) |
| O8viii—K6—O3xi | 114.38 (6) | Na1xxii—O7—Ca2 | 82.73 (7) |
| O8xiii—K6—O3xi | 118.27 (6) | Ca1xxii—O7—Ca2 | 82.73 (7) |
| O6xvi—K6—O3xi | 75.80 (7) | Na3xvii—O7—Ca2 | 105.78 (9) |
| O6xi—K6—O3xi | 55.40 (6) | Ca3xvii—O7—Ca2 | 105.78 (9) |
| O4xiii—K6—O3xi | 158.21 (6) | Si1—O7—K6xvii | 90.76 (10) |
| O4viii—K6—O3xi | 74.95 (6) | Na1xxii—O7—K6xvii | 79.35 (6) |
| O7viii—K6—O3xi | 124.58 (6) | Ca1xxii—O7—K6xvii | 79.35 (6) |
| O7xiii—K6—O3xi | 64.14 (6) | Na3xvii—O7—K6xvii | 85.89 (6) |
| O8viii—K6—O3xvi | 118.27 (6) | Ca3xvii—O7—K6xvii | 85.89 (6) |
| O8xiii—K6—O3xvi | 114.38 (6) | Ca2—O7—K6xvii | 158.23 (9) |
| O6xvi—K6—O3xvi | 55.40 (6) | Si1—O8—Si2 | 162.72 (17) |
| O6xi—K6—O3xvi | 75.80 (7) | Si1—O8—K6xvii | 98.61 (10) |
| O4xiii—K6—O3xvi | 74.95 (6) | Si2—O8—K6xvii | 98.43 (10) |
| O4viii—K6—O3xvi | 158.21 (6) | Si1—O8—K7xvii | 99.22 (12) |
| O7viii—K6—O3xvi | 64.14 (6) | Si2—O8—K7xvii | 86.99 (10) |
| O7xiii—K6—O3xvi | 124.58 (6) | K6xvii—O8—K7xvii | 78.47 (11) |
| O3xi—K6—O3xvi | 90.51 (9) | Si1—O8—Na5vii | 88.02 (11) |
| O8xiii—K7—O8viii | 101.1 (2) | Si2—O8—Na5vii | 87.57 (11) |
| O8xiii—K7—O3xiii | 112.33 (6) | K6xvii—O8—Na5vii | 95.28 (8) |
| O8viii—K7—O3xiii | 116.40 (6) | K7xvii—O8—Na5vii | 171.02 (11) |
| O8xiii—K7—O3viii | 116.40 (6) | Si1—O8—Ca5vii | 88.02 (11) |
| O8viii—K7—O3viii | 112.33 (6) | Si2—O8—Ca5vii | 87.57 (11) |
| O3xiii—K7—O3viii | 99.08 (19) | K6xvii—O8—Ca5vii | 95.28 (8) |
| O8xiii—K7—O10viii | 127.53 (15) | K7xvii—O8—Ca5vii | 171.02 (11) |
| O8viii—K7—O10viii | 56.84 (7) | Na5vii—O8—Ca5vii | 0.00 (5) |
| O3xiii—K7—O10viii | 120.12 (15) | Si1ii—O9—Si1 | 167.7 (2) |
| O3viii—K7—O10viii | 55.56 (7) | Si1ii—O9—Ca2 | 96.17 (11) |
| O8xiii—K7—O10xiii | 56.84 (7) | Si1—O9—Ca2 | 96.17 (11) |
| O8viii—K7—O10xiii | 127.53 (15) | Si1ii—O9—Ca5iv | 88.94 (4) |
| O3xiii—K7—O10xiii | 55.56 (7) | Si1—O9—Ca5iv | 90.80 (3) |
| O3viii—K7—O10xiii | 120.12 (15) | Ca2—O9—Ca5iv | 91.21 (7) |
| O10viii—K7—O10xiii | 174.4 (2) | Si1ii—O9—Na5iv | 88.94 (4) |
| O1—Si1—O7 | 119.22 (12) | Si1—O9—Na5iv | 90.80 (3) |
| O1—Si1—O8 | 112.24 (14) | Ca2—O9—Na5iv | 91.21 (7) |
| O7—Si1—O8 | 107.61 (13) | Ca5iv—O9—Na5iv | 0.00 (5) |
| O1—Si1—O9 | 106.15 (10) | Si1ii—O9—Ca5vii | 90.80 (3) |
| O7—Si1—O9 | 103.21 (14) | Si1—O9—Ca5vii | 88.94 (4) |
| O8—Si1—O9 | 107.47 (13) | Ca2—O9—Ca5vii | 91.21 (7) |
| O4—Si2—O5 | 117.33 (11) | Ca5iv—O9—Ca5vii | 177.57 (14) |
| O4—Si2—O10 | 106.19 (13) | Na5iv—O9—Ca5vii | 177.57 (14) |
| O5—Si2—O10 | 107.21 (13) | Si1ii—O9—Na5vii | 90.80 (3) |
| O4—Si2—O8 | 108.28 (12) | Si1—O9—Na5vii | 88.94 (4) |
| O5—Si2—O8 | 109.46 (13) | Ca2—O9—Na5vii | 91.21 (7) |
| O10—Si2—O8 | 107.99 (13) | Ca5iv—O9—Na5vii | 177.57 (14) |
| O6—Si3—O2 | 117.29 (12) | Na5iv—O9—Na5vii | 177.57 (14) |
| O6—Si3—O3 | 112.35 (13) | Ca5vii—O9—Na5vii | 0.00 (5) |
| O2—Si3—O3 | 107.25 (12) | Si2—O10—Si3 | 165.42 (17) |
| O6—Si3—O10 | 109.72 (15) | Si2—O10—Ca5 | 98.05 (11) |
| O2—Si3—O10 | 101.96 (13) | Si3—O10—Ca5 | 96.44 (11) |
| O3—Si3—O10 | 107.41 (12) | Si2—O10—K7xvii | 83.09 (15) |
| Si1—O1—Ca1 | 132.25 (14) | Si3—O10—K7xvii | 82.36 (14) |
| Si1—O1—Na4xvii | 123.01 (12) | Ca5—O10—K7xvii | 177.20 (12) |
| Ca1—O1—Na4xvii | 99.02 (9) | Si2—O10—Ca4xx | 89.60 (11) |
| Si1—O1—Ca4xvii | 123.01 (12) | Si3—O10—Ca4xx | 87.19 (10) |
| Ca1—O1—Ca4xvii | 99.02 (9) | Ca5—O10—Ca4xx | 96.12 (9) |
| Na4xvii—O1—Ca4xvii | 0.00 (4) | K7xvii—O10—Ca4xx | 81.32 (6) |
| Si1—O1—Na5iv | 104.50 (11) | Si2—O10—Na4xx | 89.60 (11) |
| Ca1—O1—Na5iv | 80.66 (7) | Si3—O10—Na4xx | 87.19 (10) |
| Na4xvii—O1—Na5iv | 107.14 (10) | Ca5—O10—Na4xx | 96.12 (9) |
| Ca4xvii—O1—Na5iv | 107.14 (10) | K7xvii—O10—Na4xx | 81.32 (6) |
| Si1—O1—Ca5iv | 104.50 (11) | Ca4xx—O10—Na4xx | 0.00 (4) |
| Symmetry codes: (i) −x+1, y, −z+2; (ii) y, x, −z+7/4; (iii) x, y+1, z; (iv) x−1, y, z; (v) y−1, x−1, −z+7/4; (vi) x−1, y−1, z; (vii) y, x−1, −z+7/4; (viii) −x+1, y, −z+1; (ix) x−1, y, z−1; (x) x−1, y−1, z−1; (xi) −x+1, y−1, −z+1; (xii) −x, y, −z+1; (xiii) x, y, z−1; (xiv) x+1, y, z; (xv) y+1, x, −z+7/4; (xvi) x, y−1, z−1; (xvii) x, y, z+1; (xviii) x+1, y+1, z; (xix) x+1, y+1, z+1; (xx) x+1, y, z+1; (xxi) x, y+1, z+1; (xxii) x, y−1, z. |
Acknowledgements
The authors acknowledge Dominik Messner for performing preliminary synthesis experiments. The computational results presented here have been achieved (in part) using the LEO HPC infrastructure of the University of Innsbruck.
References
Angel, R. J., Shaw, C. S. J. & Gibbs, G. V. (2003). Phys. Chem. Miner. 30, 167–176. Web of Science CrossRef ICSD CAS Google Scholar
Antao, S. M., Hassan, I., Wang, J., Lee, P. E. & Toby, B. H. (2008). Can. Mineral. 46, 1501–1509. CrossRef CAS Google Scholar
Argaman, N. & Makov, G. (2000). Am. J. Phys. 68, 69–79. CrossRef CAS Google Scholar
Arroyabe, E. & Kahlenberg, V. (2011). Eur. J. Mineral. 23, 101–110. CrossRef CAS Google Scholar
Arroyabe, E., Prechtel, F., Többens, D. M., Kaindl, R. & Kahlenberg, V. (2011). Eur. J. Mineral. 23, 425–435. CrossRef CAS Google Scholar
Averbuch-Pouchot, M. T. & Durif, A. (1996). Topics in Phosphate Chemistry, p. 404. Singapore, New Jersey, London, Hong Kong: World Scientific. Google Scholar
Bale, C. W., Bélisle, E., Chartrand, P., Decterov, S. A., Eriksson, G., Hack, K., Jung, I. H., Kang, Y. B., Melançon, J., Pelton, A. D., Robelin, C. & Petersen, S. (2009). Calphad, 33, 295–311. CrossRef CAS Google Scholar
Becke, A. D. (2014). J. Chem. Phys. 140, 18A301. Web of Science CrossRef PubMed Google Scholar
Blatov, V. A. (2012). Struct. Chem. 23, 955–963. Web of Science CrossRef CAS Google Scholar
Blatov, V. A., O'Keeffe, M. O. & Proserpio, D. M. (2010). CrystEngComm, 12, 44–48. CrossRef CAS Google Scholar
Blatov, V. A., Shevchenko, A. P. & Proserpio, D. M. (2014). Cryst. Growth Des. 14, 3576–3586. Web of Science CrossRef CAS Google Scholar
Brese, N. E. & O'Keeffe, M. (1991). Acta Cryst. B47, 192–197. CrossRef CAS Web of Science IUCr Journals Google Scholar
Brink, D. M. (2002). Nucl. Phys. News, 12, 27–32. CrossRef Google Scholar
Brown, I. D. (2016). The Chemical Bond in Inorganic Chemistry: The Bond Valence Model, 2nd ed., p. 315. Oxford University Press. Google Scholar
Brown, I. D. & Altermatt, D. (1985). Acta Cryst. B41, 244–247. CrossRef CAS Web of Science IUCr Journals Google Scholar
Burla, M. C., Camalli, M., Carrozzini, B., Cascarano, G. L., Giacovazzo, C., Polidori, G. & Spagna, R. (2003). J. Appl. Cryst. 36, 1103. Google Scholar
Chen, D. L., Stern, A. C., Space, B. & Johnson, J. K. (2010). J. Phys. Chem. A, 114, 10225–10233. CrossRef CAS PubMed Google Scholar
Clark, R. C. & Reid, J. S. (1995). Acta Cryst. A51, 887–897. CrossRef CAS Web of Science IUCr Journals Google Scholar
Demontis, P., Spanu, S. & Suffritti, G. B. (2001). J. Chem. Phys. 114, 7980–7988. CrossRef CAS Google Scholar
Dera, P., Lazarz, J. D., Prakapenka, V. B., Barkley, M. & Downs, R. T. (2011). Phys. Chem. Miner. 38, 517–529. CrossRef CAS Google Scholar
Dilmore, M. F., Clark, D. E. & Hench, L. L. (1978). J. Am. Ceram. Soc. 61, 439–443. CrossRef CAS Google Scholar
Erba, A., Desmarais, J. K., Casassa, S., Civalleri, B., Donà, L., Bush, I. J., Searle, B., Maschio, L., Edith-Daga, L., Cossard, A., Ribaldone, C., Ascrizzi, E., Marana, N. L., Flament, J. P. & Kirtman, B. (2023). J. Chem. Theory Comput. 19, 6891–6932. CrossRef CAS PubMed Google Scholar
Ewald, P. P. (1921). Annalen Phys. 369, 253–287. CrossRef Google Scholar
Fennell, C. F. & Gezelter, J. D. (2006). J. Chem. Phys. 124, 234104. CrossRef PubMed Google Scholar
Fischer, R. X. & Tillmanns, E. (1987). Acta Cryst. C43, 1852–1854. CrossRef CAS IUCr Journals Google Scholar
Flack, H. D. (1983). Acta Cryst. A39, 876–881. CrossRef CAS Web of Science IUCr Journals Google Scholar
Fukuda, I. & Nakamura, H. (2012). Biophys. Rev. 4, 161–170. CrossRef CAS PubMed Google Scholar
Gdoutos, E. E., Agrawal, R. & Espinosa, H. D. (2010). Numer. Meth Eng. 84, 1541–1551. CrossRef Google Scholar
Gramaccioli, C. M., Liborio, G. & Pilati, T. (1981). Acta Cryst. B37, 1972–1978. CrossRef CAS IUCr Journals Google Scholar
Grund, L. & Jonson, B. (2009). Glass Technol. Eur. J. Glass Sci. Technol. 50, 62–64. CAS Google Scholar
Hellenbrandt, M. (2004). Crystallogr. Rev. 10, 17–22. CrossRef CAS Google Scholar
Henry, M. (1997). Modelling of Minerals and Silicated Materials. Topics in Molecular Organization and Engineering, edited by B. Silvi & P. D'Arco, pp. 273–334. Dordrecht: Springer. Google Scholar
Hill, R. J., Newton, M. D. & Gibbs, G. V. (1983). J. Solid State Chem. 47, 185–200. CrossRef ICSD CAS Web of Science Google Scholar
Höppe, H. A. (2005). Z. Anorg. Allge Chem. 631, 1272–1276. Google Scholar
Ilyushin, G. D. & Blatov, V. A. (2002). Acta Cryst. B58, 198–218. Web of Science CrossRef CAS IUCr Journals Google Scholar
Janssens, G. O. A., Baekelandt, B. G., Toufar, H., Mortier, W. J. & Schoonheydt, R. A. (1995). J. Phys. Chem. 99, 3251–3258. CrossRef CAS Google Scholar
Jones, R. E. & Templeton, D. H. (1956). J. Chem. Phys. 25, 1062–1063. CrossRef CAS Google Scholar
Jones, R. O. (2015). Rev. Mod. Phys. 87, 897–923. Web of Science CrossRef Google Scholar
Joshi, K. L., Psofogiannakis, G., van Duin, A. C. T. & Raman, S. (2014). Phys. Chem. Chem. Phys. 16, 18433–18441. CrossRef CAS PubMed Google Scholar
Kahlenberg, V. (2001). J. Solid State Chem. 160, 421–429. Web of Science CrossRef ICSD CAS Google Scholar
Kahlenberg, V. (2002a). Mater. Res. Bull. 37, 715–726. CrossRef CAS Google Scholar
Kahlenberg, V. (2002b). Solid State Sci. 4, 183–189. CrossRef CAS Google Scholar
Kahlenberg, V. (2023). Miner. Petrol. 117, 293–306. CrossRef CAS Google Scholar
Kahlenberg, V., Girtler, D., Arroyabe, E., Kaindl, R. & Többens, D. M. (2010). Mineral. Petrol. 100, 1–9. CrossRef CAS Google Scholar
Kahlenberg, V. & Hösch, A. (2002). Z. Kristallogr. 217, 155–163. Web of Science CrossRef ICSD CAS Google Scholar
Kahlenberg, V., Mayerl, M. J. P., Schmidmair, D., Krüger, H. & Tribus, M. (2018a). Mineral. Petrol. 112, 219–228. CrossRef CAS Google Scholar
Kahlenberg, V., Mayerl, M. J. P., Schmidmair, D., Krüger, H. & Tribus, M. (2018b). Eur. J. Mineral. 30, 957–966. Web of Science CrossRef CAS Google Scholar
Kahlenberg, V., Vinke, J., Krüger, H., Ito, S. & Schürmann, C. J. (2022). J. Am. Ceram. Soc. 105, 6976–6988. CrossRef CAS Google Scholar
Kasatkin, A. V., Cámara, F., Chukanov, N. V., Škoda, R., Nestola, F., Agakhanov, A. A., Belakovskiy, D. I. & Lednyov, V. S. (2019). Minerals, 9, 611. CrossRef Google Scholar
Krüger, H., Lazić, B., Arroyabe, E. & Kahlenberg, V. (2009). Acta Cryst. B65, 587–592. CrossRef IUCr Journals Google Scholar
Kumar Kannam, S., Todd, B. D., Hansen, J. S. & Daivis, P. J. (2012). J. Chem. Phys. 136, 024705. CrossRef PubMed Google Scholar
Leven, I., Hao, H., Tan, S., Guan, X., Penrod, K. A., Akbarian, D., Evangelisti, B. Md. J., Hossain, Md. M., Islam, M. M., Koski, J. P., Moore, S. M., Aktulga, H. M., van Duin, A. C. T. & Head-Gordon, T. (2021). J. Chem. Theory Comput. 17, 3237–3251. CrossRef CAS PubMed Google Scholar
Liebau, F. (1985). Structural Chemistry of Silicates, p. 347. Berlin, Heidelberg: Springer. Google Scholar
Liu, H., Hildebrandt, E., Krammer, H., Kahlenberg, V., Krüger, H. & Schottenberger, H. (2021). J. Am. Ceram. Soc. 104, 6678–6695. CrossRef CAS Google Scholar
Momma, K. & Izumi, F. (2011). J. Appl. Cryst. 44, 1272–1276. Web of Science CrossRef CAS IUCr Journals Google Scholar
Mortier, W. J., Ghosh, S. K. & Shankar, S. (1986). J. Am. Chem. Soc. 108, 4315–4320. CrossRef CAS Google Scholar
Mortier, W. J., Van Genechten, K. & Gasteiger, J. (1985). J. Am. Chem. Soc. 107, 829–835. CrossRef CAS Google Scholar
Ozaki, Y., Beć, K. B., Morisawa, Y., Yamamoto, S., Tanabe, I., Huck, C. W. & Hofer, T. S. (2021). Chem. Soc. Rev. 50, 10917–10954. CrossRef CAS PubMed Google Scholar
Pekov, I., Krivovichev, S. V., Zolotarev, A. A., Yakovenchuk, V. N., Armbruster, T. & Pakhomovsky, Y. A. (2009). Eur. J. Mineral. 21, 1061–1071. CrossRef CAS Google Scholar
Prince, E. (2004). Editor. International Tables for X-ray Crystallography, Vol. C, Mathematical, Physical and Chemical Tables, 3rd ed. Dordrecht: Springer. Google Scholar
Rigaku Oxford Diffraction (2020). CrysAlis PRO. Rigaku Oxford Diffraction, Yarnton, England. Google Scholar
Robinson, K., Gibbs, G. V. & Ribbe, P. H. (1971). Science, 172, 567–570. CrossRef PubMed CAS Web of Science Google Scholar
Safronov, A. N., Nevskii, N. N., Ilyukhin, V. V. & Belov, N. V. (1983). Sov. Phys. Dokl. 28, 304–305. Google Scholar
Santoso, I., Taskinen, P., Jokilaakso, A., Paek, M. & Lindberg, D. (2020). Fuel, 265, 116894. CrossRef Google Scholar
Schimka, L., Harl, J. & Kresse, G. (2011). J. Chem. Phys. 134, 024116. CrossRef PubMed Google Scholar
Schleder, G. R., Padilha, A. C. M., Acosta, C. M., Costa, M. & Fazzio, A. (2019). J. Phys. Mater. 2, 032001. CrossRef Google Scholar
Schmidmair, D., Kahlenberg, V. & Grießer, A. (2018). J. Am. Ceram. Soc. 101, 919–927. Web of Science CrossRef ICSD CAS Google Scholar
Schmidmair, D., Kahlenberg, V., Praxmarer, A., Perfler, L. & Mair, P. (2017). J. Solid State Chem. 253, 336–346. CrossRef CAS Google Scholar
Senftle, T. P., Hong, S., Islam, Md. M., Kylasa, S. B., Zheng, Y., Shin, Y. K., Junkermeier, C., Engel-Herbert, R., Janik, M. J., Aktulga, H. M., Verstraelen, T., Grama, A. & van Duin, A. C. T. (2016). npj Comput. Mater. 2, 15011. CrossRef Google Scholar
Shankar, S. & Parr, R. G. (1985). Proc. Natl Acad. Sci. USA, 82, 264–266. CrossRef CAS PubMed Google Scholar
Shelby, J. E. (2005). Introduction to Glass Science and Technology, 2nd ed., p. 307. Cambridge: The Royal Society of Chemistry. Google Scholar
Sheldrick, G. M. (2015). Acta Cryst. C71, 3–8. Web of Science CrossRef IUCr Journals Google Scholar
Siidra, O. I., Zenko, D. S. & Krivovichev, S. V. (2014). Am. Mineral. 99, 817–823. Web of Science CrossRef ICSD CAS Google Scholar
Stenberg, S. & Stenqvist, B. (2020). J. Phys. Chem. A, 124, 3943–3946. CrossRef CAS PubMed Google Scholar
Takéuchi, Y., Mori, H., Kudoh, Y. & Ito, J. (1984). Acta Cryst. B40, 126–132. CrossRef IUCr Journals Google Scholar
Van Duin, A. (2009). Computational Methods in Catalysis and Materials Science: An Introduction for Scientists and Engineers, edited by R. A. van Santen & P. Sautet, pp. 167–181. Weinheim: Wiley-VCH. Google Scholar
Van Genechten, K. & Mortier, W. J. (1988). Zeolites, 8, 273–283. CrossRef CAS Google Scholar
Van Genechten, K., Mortier, W. J. & Geerlings, P. (1987). J. Chem. Phys. 86, 5063–5071. CrossRef CAS Google Scholar
Vassilev, S. V., Baxter, D., Andersen, L. K. & Vassileva, C. G. (2013). Fuel, 105, 40–76. CrossRef CAS Google Scholar
Verstraelen, T., Sukhomlinov, S. V., van Speybroeck, V., Waroquier, M. & Smirnov, K. S. (2012). J. Phys. Chem. C116, 490–504. Google Scholar
Vilela Oliveira, D., Laun, J., Peintinger, M. F. & Bredow, T. (2019). J. Comput. Chem. 40, 2364–2376. Web of Science CrossRef CAS PubMed Google Scholar
Viveros-Méndez, P. X. & Gil-Villegas, A. (2012). J. Chem. Phys. 136, 154507. PubMed Google Scholar
Wierzbicka-Wieczorek, M., Kolitsch, U. & Tillmanns, E. (2010a). Eur. J. Mineral. 22, 245–258. CAS Google Scholar
Wierzbicka-Wieczorek, M., Kolitsch, U. & Tillmanns, E. (2010b). Acta Cryst. C66, i29–i32. Web of Science CrossRef ICSD IUCr Journals Google Scholar
Wolf, D., Keblinski, P., Phillpot, S. R. & Eggebrecht, J. (1999). J. Chem. Phys. 110, 8254–8282. Web of Science CrossRef CAS Google Scholar
Wolters, M. A. & Braun, W. J. (2018). Stat, 7, e202. CrossRef Google Scholar
Yu, H. S., Li, S. L. & Truhlar, D. G. (2016). J. Chem. Phys. 145, 130901. CrossRef PubMed Google Scholar
Zahn, D., Schilling, B. & Kast, S. M. (2002). J. Phys. Chem. B, 106, 10725–10732. Web of Science CrossRef CAS Google Scholar
This is an open-access article distributed under the terms of the Creative Commons Attribution (CC-BY) Licence, which permits unrestricted use, distribution, and reproduction in any medium, provided the original authors and source are cited.