Comparison between diffraction contrast tomography and high-energy diffraction microscopy on a slightly deformed aluminium alloy

Renversade, L.; Quey, R.; Ludwig, W.; Menasche, D.; Maddali, S.; Suter, R.M.; Borbély, A.

doi:10.1107/S2052252515019995

Figure 8
Comparison of far-field 3DXRD results with the HEDM map of layer No. 3. 81 grains obtained from far-field data are represented as black circles centred on the estimated grain centre-of-mass position; the radii are proportional to the grain sizes obtained from far-field intensities (downscaled for the sake of visibility). Only a few differences can be observed, mainly in the subgrain aggregates on the right-hand side of the map. The white asterisk marks the grain analysed in Fig. 7