Supporting information
Crystallographic Information File (CIF) https://doi.org/10.1107/S1600536806002406/hk6079sup1.cif | |
Structure factor file (CIF format) https://doi.org/10.1107/S1600536806002406/hk6079Isup2.hkl |
CCDC reference: 298469
Key indicators
- Single-crystal X-ray study
- T = 294 K
- Mean (C-C) = 0.004 Å
- R factor = 0.041
- wR factor = 0.136
- Data-to-parameter ratio = 14.8
checkCIF/PLATON results
No syntax errors found
Alert level C PLAT021_ALERT_1_C Ratio Unique / Expected Reflections too High ... 1.03 PLAT066_ALERT_1_C Predicted and Reported Transmissions Identical . ?
0 ALERT level A = In general: serious problem 0 ALERT level B = Potentially serious problem 2 ALERT level C = Check and explain 0 ALERT level G = General alerts; check 2 ALERT type 1 CIF construction/syntax error, inconsistent or missing data 0 ALERT type 2 Indicator that the structure model may be wrong or deficient 0 ALERT type 3 Indicator that the structure quality may be low 0 ALERT type 4 Improvement, methodology, query or suggestion
checkCIF publication errors
Alert level A PUBL023_ALERT_1_A There is a mismatched ^ on line 390 Refinement of F2^ against ALL reflections. The weighted R-factor wR and If you require a ^ then it should be escaped with a \, i.e. \^ Otherwise there must be a matching closing ~, e.g. ^12^C PUBL023_ALERT_1_A There is a mismatched ^ on line 391 goodness of fit S are based on F2^, conventional R-factors R are based If you require a ^ then it should be escaped with a \, i.e. \^ Otherwise there must be a matching closing ~, e.g. ^12^C PUBL023_ALERT_1_A There is a mismatched ^ on line 392 on F, with F set to zero for negative F2^. The threshold expression of If you require a ^ then it should be escaped with a \, i.e. \^ Otherwise there must be a matching closing ~, e.g. ^12^C PUBL023_ALERT_1_A There is a mismatched ^ on line 395 on F2^ are statistically about twice as large as those based on F, and R- If you require a ^ then it should be escaped with a \, i.e. \^ Otherwise there must be a matching closing ~, e.g. ^12^C PUBL023_ALERT_1_A There is a mismatched ^ on line 404 'w = 1/[\s2^(Fo2^)+(0.0679P)2^+0.8662P] where P=(Fo2^+2Fc2^)/3' If you require a ^ then it should be escaped with a \, i.e. \^ Otherwise there must be a matching closing ~, e.g. ^12^C
5 ALERT level A = Data missing that is essential or data in wrong format 0 ALERT level G = General alerts. Data that may be required is missing
Data collection: SMART (Bruker, 1997); cell refinement: SMART; data reduction: SAINT (Bruker, 1997); program(s) used to solve structure: SHELXS97 (Sheldrick, 1997); program(s) used to refine structure: SHELXL97 (Sheldrick, 1997); molecular graphics: SHELXTL (Bruker, 1997); software used to prepare material for publication: SHELXTL.
C13H11NO6S | Dx = 1.485 Mg m−3 |
Mr = 309.30 | Melting point: 361 K |
Orthorhombic, Pbca | Mo Kα radiation, λ = 0.71073 Å |
Hall symbol: -P 2ac 2ab | Cell parameters from 3444 reflections |
a = 6.2331 (9) Å | θ = 2.6–23.8° |
b = 16.000 (2) Å | µ = 0.26 mm−1 |
c = 27.741 (4) Å | T = 294 K |
V = 2766.6 (7) Å3 | Block, colourless |
Z = 8 | 0.26 × 0.24 × 0.12 mm |
F(000) = 1280 |
Bruker 1000 CCD area-detector diffractometer | 2830 independent reflections |
Radiation source: fine-focus sealed tube | 1547 reflections with I > 2σ(I) |
Graphite monochromator | Rint = 0.039 |
φ and ω scans | θmax = 26.4°, θmin = 1.5° |
Absorption correction: multi-scan (SADABS; Sheldrick, 1996) | h = −7→7 |
Tmin = 0.935, Tmax = 0.969 | k = −19→19 |
14390 measured reflections | l = −34→17 |
Refinement on F2 | Primary atom site location: structure-invariant direct methods |
Least-squares matrix: full | Secondary atom site location: difference Fourier map |
R[F2 > 2σ(F2)] = 0.042 | Hydrogen site location: inferred from neighbouring sites |
wR(F2) = 0.136 | H-atom parameters constrained |
S = 1.00 | w = 1/[σ2(Fo2) + (0.0679P)2 + 0.8662P] where P = (Fo2 + 2Fc2)/3 |
2830 reflections | (Δ/σ)max = 0.001 |
191 parameters | Δρmax = 0.23 e Å−3 |
12 restraints | Δρmin = −0.30 e Å−3 |
Geometry. All e.s.d.'s (except the e.s.d. in the dihedral angle between two l.s. planes) are estimated using the full covariance matrix. The cell e.s.d.'s are taken into account individually in the estimation of e.s.d.'s in distances, angles and torsion angles; correlations between e.s.d.'s in cell parameters are only used when they are defined by crystal symmetry. An approximate (isotropic) treatment of cell e.s.d.'s is used for estimating e.s.d.'s involving l.s. planes. |
Refinement. Refinement of F2 against ALL reflections. The weighted R-factor wR and goodness of fit S are based on F2, conventional R-factors R are based on F, with F set to zero for negative F2. The threshold expression of F2 > σ(F2) is used only for calculating R-factors(gt) etc. and is not relevant to the choice of reflections for refinement. R-factors based on F2 are statistically about twice as large as those based on F, and R- factors based on ALL data will be even larger. |
x | y | z | Uiso*/Ueq | ||
S1 | 0.24533 (11) | 0.53721 (4) | 0.16281 (2) | 0.0527 (2) | |
O1 | 0.4535 (3) | 0.55580 (12) | 0.14504 (7) | 0.0673 (5) | |
O2 | 0.2171 (4) | 0.47795 (12) | 0.20009 (7) | 0.0760 (6) | |
O3 | 0.1081 (3) | 0.49767 (10) | 0.11896 (6) | 0.0580 (5) | |
O4 | 0.3660 (3) | 0.60083 (17) | −0.02989 (8) | 0.0889 (7) | |
H4 | 0.3303 | 0.6295 | −0.0530 | 0.133* | |
O5 | 0.1007 (5) | 0.69237 (17) | −0.07802 (8) | 0.1012 (8) | |
O6 | −0.2130 (5) | 0.72121 (18) | −0.04984 (10) | 0.1190 (10) | |
N1 | −0.0392 (5) | 0.68604 (18) | −0.04673 (10) | 0.0779 (7) | |
C1 | 0.1076 (4) | 0.62943 (14) | 0.17497 (8) | 0.0419 (6) | |
C2 | 0.1914 (4) | 0.70479 (15) | 0.15977 (9) | 0.0509 (6) | |
H2 | 0.3242 | 0.7069 | 0.1445 | 0.061* | |
C3 | 0.0757 (5) | 0.77672 (16) | 0.16751 (9) | 0.0584 (7) | |
H3 | 0.1323 | 0.8276 | 0.1575 | 0.070* | |
C4 | −0.1229 (4) | 0.77533 (16) | 0.18985 (9) | 0.0535 (7) | |
C5 | −0.2023 (4) | 0.69885 (17) | 0.20520 (9) | 0.0543 (7) | |
H5 | −0.3348 | 0.6969 | 0.2206 | 0.065* | |
C6 | −0.0894 (4) | 0.62558 (16) | 0.19820 (9) | 0.0503 (6) | |
H6 | −0.1442 | 0.5747 | 0.2088 | 0.060* | |
C7 | −0.2495 (6) | 0.85419 (19) | 0.19764 (12) | 0.0813 (10) | |
H7A | −0.2286 | 0.8735 | 0.2301 | 0.122* | |
H7B | −0.3990 | 0.8432 | 0.1924 | 0.122* | |
H7C | −0.2016 | 0.8963 | 0.1754 | 0.122* | |
C8 | 0.0791 (4) | 0.54601 (14) | 0.07732 (9) | 0.0487 (6) | |
C9 | −0.1193 (4) | 0.58438 (18) | 0.07118 (10) | 0.0597 (7) | |
H9 | −0.2259 | 0.5796 | 0.0945 | 0.072* | |
C10 | −0.1533 (4) | 0.62911 (19) | 0.03021 (11) | 0.0637 (8) | |
H10 | −0.2852 | 0.6549 | 0.0252 | 0.076* | |
C11 | 0.0052 (5) | 0.63660 (16) | −0.00393 (10) | 0.0559 (7) | |
C12 | 0.2037 (4) | 0.59743 (18) | 0.00205 (10) | 0.0572 (7) | |
C13 | 0.2378 (4) | 0.55128 (16) | 0.04362 (10) | 0.0550 (7) | |
H13 | 0.3679 | 0.5241 | 0.0485 | 0.066* |
U11 | U22 | U33 | U12 | U13 | U23 | |
S1 | 0.0503 (4) | 0.0493 (4) | 0.0583 (4) | 0.0026 (3) | 0.0015 (3) | 0.0045 (3) |
O1 | 0.0434 (10) | 0.0768 (13) | 0.0815 (13) | 0.0031 (9) | 0.0042 (10) | −0.0001 (11) |
O2 | 0.0905 (15) | 0.0606 (12) | 0.0770 (13) | 0.0106 (11) | 0.0018 (12) | 0.0236 (11) |
O3 | 0.0640 (11) | 0.0453 (10) | 0.0647 (11) | −0.0078 (9) | 0.0043 (9) | −0.0063 (9) |
O4 | 0.0628 (13) | 0.129 (2) | 0.0754 (15) | 0.0072 (13) | 0.0163 (12) | 0.0107 (14) |
O5 | 0.111 (2) | 0.123 (2) | 0.0695 (14) | −0.0054 (17) | −0.0011 (15) | 0.0108 (14) |
O6 | 0.122 (2) | 0.134 (2) | 0.1013 (19) | 0.0520 (19) | −0.0160 (17) | 0.0158 (17) |
N1 | 0.090 (2) | 0.0789 (18) | 0.0648 (17) | 0.0025 (16) | −0.0107 (17) | −0.0103 (15) |
C1 | 0.0430 (13) | 0.0440 (13) | 0.0388 (12) | −0.0043 (10) | 0.0004 (10) | −0.0004 (10) |
C2 | 0.0493 (14) | 0.0506 (15) | 0.0528 (14) | −0.0074 (11) | 0.0113 (12) | −0.0004 (12) |
C3 | 0.0708 (18) | 0.0427 (14) | 0.0617 (16) | −0.0087 (13) | 0.0079 (15) | −0.0002 (12) |
C4 | 0.0611 (18) | 0.0555 (16) | 0.0439 (14) | 0.0046 (13) | −0.0046 (13) | −0.0116 (12) |
C5 | 0.0456 (14) | 0.0711 (18) | 0.0462 (14) | −0.0021 (13) | 0.0068 (12) | −0.0082 (13) |
C6 | 0.0492 (14) | 0.0539 (15) | 0.0477 (14) | −0.0092 (12) | 0.0031 (12) | 0.0021 (12) |
C7 | 0.095 (2) | 0.0711 (19) | 0.078 (2) | 0.0217 (18) | −0.0003 (19) | −0.0188 (17) |
C8 | 0.0485 (14) | 0.0436 (13) | 0.0541 (15) | −0.0014 (11) | 0.0015 (12) | −0.0173 (12) |
C9 | 0.0441 (15) | 0.0787 (19) | 0.0563 (16) | 0.0018 (13) | 0.0037 (13) | −0.0197 (15) |
C10 | 0.0492 (16) | 0.0773 (19) | 0.0646 (18) | 0.0149 (14) | −0.0069 (15) | −0.0245 (16) |
C11 | 0.0603 (16) | 0.0555 (15) | 0.0520 (15) | 0.0014 (13) | −0.0087 (14) | −0.0148 (13) |
C12 | 0.0494 (16) | 0.0682 (17) | 0.0542 (15) | −0.0033 (13) | 0.0068 (13) | −0.0156 (14) |
C13 | 0.0431 (14) | 0.0583 (16) | 0.0637 (16) | 0.0054 (12) | 0.0044 (13) | −0.0146 (13) |
S1—O2 | 1.4142 (19) | C4—C7 | 1.504 (4) |
S1—O1 | 1.4195 (19) | C5—C6 | 1.381 (4) |
S1—O3 | 1.6160 (18) | C5—H5 | 0.9300 |
S1—C1 | 1.740 (2) | C6—H6 | 0.9300 |
O3—C8 | 1.402 (3) | C7—H7A | 0.9600 |
O4—C12 | 1.346 (3) | C7—H7B | 0.9600 |
O4—H4 | 0.8200 | C7—H7C | 0.9600 |
O5—N1 | 1.234 (3) | C8—C13 | 1.364 (3) |
O6—N1 | 1.224 (4) | C8—C9 | 1.391 (4) |
N1—C11 | 1.453 (4) | C9—C10 | 1.360 (4) |
C1—C2 | 1.380 (3) | C9—H9 | 0.9300 |
C1—C6 | 1.388 (3) | C10—C11 | 1.374 (4) |
C2—C3 | 1.375 (3) | C10—H10 | 0.9300 |
C2—H2 | 0.9300 | C11—C12 | 1.397 (4) |
C3—C4 | 1.385 (4) | C12—C13 | 1.386 (4) |
C3—H3 | 0.9300 | C13—H13 | 0.9300 |
C4—C5 | 1.387 (4) | ||
O2—S1—O1 | 120.55 (12) | C5—C6—H6 | 120.7 |
O2—S1—O3 | 102.84 (11) | C1—C6—H6 | 120.7 |
O1—S1—O3 | 107.73 (11) | C4—C7—H7A | 109.5 |
O2—S1—C1 | 111.42 (12) | C4—C7—H7B | 109.5 |
O1—S1—C1 | 109.92 (12) | H7A—C7—H7B | 109.5 |
O3—S1—C1 | 102.52 (10) | C4—C7—H7C | 109.5 |
C8—O3—S1 | 118.20 (14) | H7A—C7—H7C | 109.5 |
C12—O4—H4 | 109.5 | H7B—C7—H7C | 109.5 |
O6—N1—O5 | 122.5 (3) | C13—C8—C9 | 122.2 (3) |
O6—N1—C11 | 118.5 (3) | C13—C8—O3 | 120.4 (2) |
O5—N1—C11 | 119.0 (3) | C9—C8—O3 | 117.3 (2) |
C2—C1—C6 | 121.0 (2) | C10—C9—C8 | 118.2 (3) |
C2—C1—S1 | 119.64 (19) | C10—C9—H9 | 120.9 |
C6—C1—S1 | 119.27 (18) | C8—C9—H9 | 120.9 |
C3—C2—C1 | 119.0 (2) | C9—C10—C11 | 120.7 (3) |
C3—C2—H2 | 120.5 | C9—C10—H10 | 119.7 |
C1—C2—H2 | 120.5 | C11—C10—H10 | 119.7 |
C2—C3—C4 | 121.7 (2) | C10—C11—C12 | 121.1 (3) |
C2—C3—H3 | 119.2 | C10—C11—N1 | 118.3 (3) |
C4—C3—H3 | 119.2 | C12—C11—N1 | 120.7 (3) |
C3—C4—C5 | 118.1 (2) | O4—C12—C13 | 117.0 (2) |
C3—C4—C7 | 121.3 (3) | O4—C12—C11 | 124.7 (3) |
C5—C4—C7 | 120.6 (3) | C13—C12—C11 | 118.3 (2) |
C6—C5—C4 | 121.6 (2) | C8—C13—C12 | 119.5 (2) |
C6—C5—H5 | 119.2 | C8—C13—H13 | 120.3 |
C4—C5—H5 | 119.2 | C12—C13—H13 | 120.3 |
C5—C6—C1 | 118.6 (2) | ||
O2—S1—O3—C8 | 172.30 (18) | S1—O3—C8—C13 | 80.1 (2) |
O1—S1—O3—C8 | −59.37 (19) | S1—O3—C8—C9 | −102.8 (2) |
C1—S1—O3—C8 | 56.56 (18) | C13—C8—C9—C10 | −0.6 (4) |
O2—S1—C1—C2 | 146.6 (2) | O3—C8—C9—C10 | −177.7 (2) |
O1—S1—C1—C2 | 10.3 (2) | C8—C9—C10—C11 | −0.5 (4) |
O3—S1—C1—C2 | −104.0 (2) | C9—C10—C11—C12 | 1.1 (4) |
O2—S1—C1—C6 | −35.9 (2) | C9—C10—C11—N1 | −179.2 (2) |
O1—S1—C1—C6 | −172.17 (18) | O6—N1—C11—C10 | 2.4 (4) |
O3—S1—C1—C6 | 73.5 (2) | O5—N1—C11—C10 | −179.0 (3) |
C6—C1—C2—C3 | −0.6 (4) | O6—N1—C11—C12 | −178.0 (3) |
S1—C1—C2—C3 | 176.8 (2) | O5—N1—C11—C12 | 0.6 (4) |
C1—C2—C3—C4 | −0.4 (4) | C10—C11—C12—O4 | 179.2 (3) |
C2—C3—C4—C5 | 1.0 (4) | N1—C11—C12—O4 | −0.5 (4) |
C2—C3—C4—C7 | −179.3 (3) | C10—C11—C12—C13 | −0.6 (4) |
C3—C4—C5—C6 | −0.7 (4) | N1—C11—C12—C13 | 179.8 (2) |
C7—C4—C5—C6 | 179.6 (2) | C9—C8—C13—C12 | 1.1 (4) |
C4—C5—C6—C1 | −0.3 (4) | O3—C8—C13—C12 | 178.2 (2) |
C2—C1—C6—C5 | 1.0 (4) | O4—C12—C13—C8 | 179.7 (2) |
S1—C1—C6—C5 | −176.44 (19) | C11—C12—C13—C8 | −0.5 (4) |
D—H···A | D—H | H···A | D···A | D—H···A |
O4—H4···O5 | 0.82 | 1.88 | 2.581 (3) | 143 |
O4—H4···N1 | 0.82 | 2.48 | 2.908 (4) | 114 |
Subscribe to Acta Crystallographica Section E: Crystallographic Communications
The full text of this article is available to subscribers to the journal.
- Information on subscribing
- Sample issue
- If you have already subscribed, you may need to register