Magnetic X-ray absorption fine structure for Ni–Mn alloys
aFaculty of Science and Technology, Hirosaki University, Hirosaki Aomori 036-8561, Japan, and bGraduate School for Science, Chiba University, Yayoi, Inage, Chiba 263-8522, Japan
*Correspondence e-mail: takaf@cc.hirosaki-u.ac.jp
Magnetic X-ray absorption fine-structure (XAFS) spectra have been measured for Ni–Mn alloys. The magnetic K-edge for Ni1−xMnx (x = 0.25, 0.24 and 0.20) show that (i) the local magnetic structure around the Mn atom is quite different from that around the Ni atom, and (ii) the peak intensity in the magnetic XANES of the Mn K-edge depends on the magnetization of the sample in contrast to the Ni K-edge. The Mn K-edge magnetic (extended XAFS) for Ni0.76Mn0.24 is also measured. The second and fourth peaks in the Fourier transform are observed to be enhanced in comparison with the non-magnetic indicating that the second- and fourth-shell Ni atoms are replaced by Mn atoms due to heat treatment (atomic ordering). Semi-relativistic theoretical calculation explains the observed magnetic EXAFS.
in the near-edge region (X-ray absorption near-edge structure, XANES) and X-ray (XMCD) of the Mn and NiKeywords: XAFS; magnetic XAFS; XMCD; Ni–Mn alloy.
1. Introduction
The correlation between the structure and magnetism of 3d transition-metal alloys has long been an important topic in condensed matter physics. Among the 3d transition-metal alloys, the Mn-based alloys have recently attracted special attention because of their potential applications in the magnetic recording technology. A particular problem of the magnetism of transition-metal alloys is the formation of the on the Mn atom, since it is closely related to the structure of the alloy under study. An interesting example of such an alloy is Ni3Mn, which forms an ordered phase of the type Cu3Au with appropriate heat treatment. Ni3Mn alloy can undergo the structural and the magnetic behaviour is sensitive to the atomic arrangement (Okazaki, 1995). Ordered Ni3Mn is a typical ferromagnetic substance with Tc
730 K and where the local moment of the Mn atom and the Ni atom is
3.5 μB and
0.31 μB, respectively (Paoletti & Ricci, 1963
). The magnetic structure in the Ni3Mn alloy is explained as a result of ferromagnetic Ni–Ni, Ni–Mn and antiferromagnetic Mn–Mn first-nearest-neighbour (1NN) interactions and ferromagnetic Mn–Mn second-nearest-neighbour (2NN) interactions (Sato et al., 1978
); only the J MnMn(1NN) interaction is antiferromagnetic. As a result, the alloy becomes a ferromagnetic material with the local of Mn being
3.5 μB. However, the values on each atom in the disordered state are not known. Cable & Child (1974
) studied the distributions in disordered NixMn1−x (x = 0.80–0.95) alloys by the polarized-neutron diffuse-scattering method. They showed that the of an isolated Mn atom in Ni0.95Mn0.05 alloy is 3.50 μB at 4.2 K and that the decreases as the concentration of Mn increases and as the temperature increases. Two possible reasons were pointed out for the decreasing of the Mn magnetic moments: (i) the ferromagnetic component of the Mn moment vanishes by becoming randomly oriented or by becoming antiferromagnetically coupled; (ii) averaging over up-spin and down-spin magnetic configurations. They concluded that the magnetic distribution is complicated and not specifically defined by the neutron measurement. We can only say that the average magnetization is small compared with that in the ordered state of Ni3Mn alloy. Since the neutron-scattering technique is based on the long-range order, we cannot say whether the net local moment of the Mn atom decreases or partially antiferromagnetic blocks are made under the conditions where the local moment of Mn is conserved even in the disordered state (Menshikov, 1999
).
In order to study the magnetic structure in the process of the ordered–disordered transition, it is important to determine the short-range order on the atomic scale. The short-range order of Ni–Mn alloys has been studied by using extended et al., 1995; Miyanaga, Okazaki, Ikeda & Kon, 1999
; Miyanaga, Okazaki, Babanov & Ryazhkin, 1999
; Ryazhkin et al., 2001
). However, it is generally difficult to distinguish the contribution of the Mn and Ni atoms by the conventional curve-fitting method because the k-dependence of the phase shifts and backscattering amplitudes of the Mn and Ni atoms are quite similar to each other. To overcome this difficulty, the small difference in the peak intensities between the Mn and Ni K-edge Fourier transforms was used for determining the short-range order (Nakahata et al., 1995
; Miyanaga, Okazaki, Ikeda & Kon, 1999
). More recently, an inverse problem was introduced to the analyses of the of Ni–Mn alloys (Miyanaga, Okazaki, Babanov & Ryazhkin, 1999
; Ryazhkin et al., 2001
). On the other hand, magnetic is a powerful tool for investigating the local magnetic structures with short-range order in the alloys, using a circular-polarized X-ray beam from a synchrotron radiation source (Schutz et al., 1987
; Lovesey & Collins, 1996
).
In this paper we study the magnetic 1−xMnx alloys (x = 0.25, 0.24, 0.20) prepared by heat treatment for structure ordering. The amplitude of the K-edge XMCD spectrum is much smaller than that of the corresponding L2,3-edge spectrum since the weak spin–orbit interaction in the diffuse 4p or photoelectron p-wave is one of the main sources of the effect. The interpretation of the magnetic XANES spectra is not so easy because they are related to both the electronic states and atomic structures. There are two approaches to analyzing the magnetic XANES: full relativistic band calculation (Ebert, 1992) and multiple-scattering theory (Brouder et al., 1996
; Nagamatsu & Fujikawa, 2001
). On the other hand, the interpretation of the magnetic is clear and direct for the study of the local magnetic structures, although the signal is much smaller than that of magnetic XANES. Recently, some theoretical approaches have been developed for the magnetic analyses (Ankdinov & Rehr, 1995
; Popescu et al., 1999
; Nagamatsu & Fujikawa, 2001
). We apply the short- and long-range-order theoretical approaches to the magnetic analyses for the binary alloy system. In §2
we present the experimental details for the magnetic XANES and the magnetic measurements. In §3
we describe the method for calculating the magnetic and electronic structure. In §4
we first discuss the experimental results of magnetic XANES for Ni1−xMnx (x = 0.25, 0.24, 0.20) alloys, then we show the experimental results of the magnetic for Ni0.76Mn0.24 alloy and analyze them by semi-relativistic theoretical calculations.
2. Experimental
2.1. Measurement of magnetic XANES
99.99% pure Ni1−xMnx (x = 0.25, 0.24, 0.20) alloys were prepared from an RF induction furnace. The powder samples of Ni1−xMnx (x = 0.25, 0.24, 0.20) were annealed for 140 h at 693 K under an Ar atmosphere in order to make certain an ordered state.
The magnetization curves for these samples were measured using a vibration sample magnetometer. The saturation magnetizations obtained from the magnetization curves at room temperature were 59 e.m.u. g−1 for Ni0.75Mn0.25, 55 e.m.u. g−1 for Ni0.76Mn0.24 and 35 e.m.u. g−1 for Ni0.80Mn0.20 alloys. The atomic structures were checked by X-ray powder diffraction and non-magnetic The short-range-order parameters for these samples were obtained from the relation between the magnetization and the X-ray diffraction peaks (Nakahata et al., 1995). The powdered samples were mounted uniformly on adhesive tape for the magnetic measurements.
The K-edge magnetic XANES spectra (about 50 eV around the K-edge of Ni and Mn) were obtained in transmission mode at BL39XU at SPring-8. X-rays from a 8 GeV storage ring (current ∼50 mA) were monochromated using an Si(111) double-crystal monochromator and then circularly polarized using a diamond (111) X-ray phase retarder. The synthetic diamond (111) crystal slab, 0.5 mm in thickness, was operated around the 220 reflection in transmission Laue geometry. A piezoelectric vibrator working at 40 Hz alternated between offset angles so as to produce a π/4 phase shift. The degree of polarization, Pc, was 0.99. Higher harmonics in the incident X-rays were rejected by inserting a Pt-coated Si mirror at θ = 5 mrad for both Ni and Mn K-edges. The XMCD signals were detected by ionization chambers filled with N2 gas using a helicity-modulation technique utilizing a lock-in amplifier. The sample plane was inclined at 45° from the X-ray beam direction. A more detailed description of the experimental set-up of BL39XU is given elsewhere (Suzuki et al., 1999). Measurements of the XMCD spectra were taken at room temperature under a magnetic field of about 1.2 T, which is strong enough to saturate the magnetization of the present samples.
2.2. Measurement of magnetic EXAFS
A 21 µm foil sample of Ni0.76Mn0.24 was prepared, polishing carefully and annealing for 100 h at 693 K under an Ar atmosphere in order to make certain an ordered state. The saturation magnetization of this sample was 56.4 e.m.u. g−1 and the proportion of the ordered state was deduced to be about 74%. Magnetic of the Mn K-edge (6.4–7.2 keV) for the Ni0.76Mn0.24 foil was measured at BL28B of the Photon Factory, KEK (2.5 GeV), with circularly polarized X-rays that were generated by an ellipsoid multipole wiggler and monochromated using an Si(111) double-crystal monochromator (Iwazumi et al., 1995; Kobayashi et al., 1996
). The absorption spectra were measured in transmission mode at 30 K. The XMCD signals were detected by ionization chambers filled with N2 gas. Instead of switching the helicity of the incident photons, the applied magnetic field, about 0.6 T, which is still sufficient to saturate the magnetization of the sample, was reserved every 4 s to obtain a effect. The angle between the surface of the sample and applied magnetic fields was tilted by 45° along the incident beam. The absorption profiles were measured as μ+(E) and μ–(E) for each direction of the applied magnetic field.
3. Theory
3.1. Theory of magnetic EXAFS
The details of the present theoretical approach are discussed elsewhere (Fujikawa & Nagamatsu, 2002); a short summary is given here for the later discussion.
In the analysis of XMCD spectra, the full potential for an excited photoelectron is written as the sum of each atomic potential,
where is the atomic potential at site
(Rα), which is assumed to be spherical symmetric for simplicity except for the spin–orbit (SO) coupling term. As a relativistic correction we take only the SO coupling into account in the two-spinor formula, which yields
where is the Coulomb potential,
is the spin-dependent exchange potential and
is the optical potential due to many-body effects (Fujikawa et al., 1998
, 2000
; Hatada et al., 2001
). The fourth term is the SO coupling potential. For light atoms, such as Mn and Ni, this term is much weaker than
=
.
Hereafter our attention is focused on light-element systems, and the SO coupling term can be treated as a weak perturbation, ,
The scattering Green's function, , for the scattering potential,
, is diagonalized because it does not contribute to the spin–flip processes,
where denotes the up (+) and down (−) spin Green's function which is written in terms of
and the operator Te,
.
We can construct the full Green's function at site in a 2 × 2 matrix,
As usual we can utilize the site T-matrix expansion of the full Green's function (Fujikawa, 1993),
where is the site T-matrix at site
which is related to
,
=
, and g0 is the free propagation and is different from
. For the randomly oriented systems considered here, the XMCD simply follows
, where
= T(1,1)-T(-1,-1) and
is the angle between the X-ray incidence and the spin axis (
). In this case, the electron–photon interaction operator
is given by
=
(mp = −1, 0, 1) neglecting unimportant constants, and we define
in terms of the 1s core spinor function,
, and the full Green's function, g,
Here Tr means the diagonal sum over the spin up and down states. Each of is written as the sum of atomic term T(0), single-scattering term T(1), and double-scattering term T(2), and so on,
The atomic X-ray absorption intensity T(0) is only important in the near-edge region (Fujikawa & Nagamatsu, 2002). Our attention is focused on the region, and we can neglect this term. By applying the site T-matrix expansion, we can write the single scattering X-ray absorption intensity
up to the first order of
which is dominated by the spin-conserved scattering processes. The lowest-order terms in the order of
0 are most important in discussing the main features of the spectra. By use of a symmetry relation (Fujikawa et al., 1997
), these are cancelled out in ΔT(1) = T(1)(1, 1) − T(1)(−1, −1). It is important to note that ΔT(1) vanishes if both the X-ray absorbing atom A and the surrounding atoms α's are non-magnetic.
3.2. FLAPW band calculation
In order to calculate the electronic structure for the phase shift in the magnetic ) is used. The scalar relativistic effects other than the spin–orbit interaction are included for all electrons. We introduce practically the muffin-tin (MT) sphere around each atom, but the potential is determined fully self-consistently over the entire crystal both inside and outside the MT spheres. The core electrons are treated as relaxed. A self-consistent potential is given from eigen states at sampling 20 k-points in the irreducible (IBZ), calculated with the basis functions truncated at |k + Gi|
5.15(2π/a), where Gi is the vector, corresponding to 587 LAPW functions at the Γ point. To obtain a final band structure, eigen energies are calculated at 455 k-points in the IBZ. For the band-structure calculations, we used the programs TSPACE (Yanase, 1995
) and KANSAI99.
In the calculation of the magnetic state, the starting crystal charge density is obtained by superposition of self-consistent charge densities for neutral atoms in which the Ni and Mn atoms are in the spin-polarized states; the d54s1 (up spin) and …3d34s1 (down spin), and that of Mn is …3d54s1 (up spin) and …3d04s1 (down spin).
of Ni is …3Partial and total densities of states are calculated using a linearly energy-interpolated tetrahedron method. The number of valence electrons in the MT spheres are calculated from the partial densities of states (and listed in Table 1).
|
The model atomic structure for Ni3Mn is AuCu3-type simple cubic for simplicity as a first step. The is Pm3m (#221, Oh1) with Mn in 1a:(0,0,0) and Ni in 3c:(1,,
). The value of the lattice constant used in the calculation is the experimental one in the well annealed Ni3Mn sample (a = 3.586 A).
4. Results and discussion
4.1. Results in the magnetic XANES (XMCD)
Fig. 1 shows the magnetic XANES (XMCD) normalized by edge jumps of non-magnetic XANES for the Mn K-edges (a) and Ni K-edge (b) in Ni0.75Mn0.25 alloy. Each non-magnetic XANES is also shown by a dotted line. In Fig. 1
(a) (Mn K-edge) we find a sharp positive peak (A) and negative peaks (B, C, D). In Fig. 1
(b) (Ni K-edge) three distinct negative peaks (E, F, G) are observed. There is no positive peak in the Ni K-edge as observed in the well known XMCD spectrum for pure Ni. The three peaks (E, F, G) in the Ni–Mn alloys are typical structures, which can be observed in pure Ni, and they are more prominent for the Ni–Mn alloys than for pure Ni.
![]() | Figure 1 XMCD spectra normalized by edge jumps of non-magnetic XANES for (a) the Mn K-edge and (b) the Ni K-edge in Ni0.75Mn0.25 alloy. The dashed line represents non-magnetic XANES. |
This result shows that the XMCD for the Mn K-edge is quite different from that for the Ni K-edge, although the XANES on both edges are similar. Magnetism in Ni–Mn alloys is considered to arise mainly from the ferromagnetic Ni3Mn ordered phase. The local environment around an Mn atom is different from that around a Ni atom in the ordered Ni3Mn alloy: 12 Ni atoms are located around one Mn atom; on the other hand, four Mn and eight Ni atoms are located around one Ni atom. Since the XMCD is a local probe of magnetic structures, the present result clearly shows the difference in the local magnetic structures around the Mn and Ni atoms in the Ni–Mn alloys. This result is in contrast to the previous result for Ni–Fe alloys (Sakurai et al., 1995). In the case of the Ni–Fe alloys, the XMCD for both K-edges of Ni and Fe are quite similar: the final 4p states hybridized with 3d states are not localized within a specific atom but are extended over the surrounding atoms.
Fig. 2 shows the variation of the peak intensities A, B, C and D in the XMCD for the Mn K-edge (a) and E, F, G for the Ni K-edge (b) as a function of the magnetization (or concentration of the Mn atom) of the sample. The peak intensity of the positive peak A depends on the magnetization of the sample (or the concentration of the Mn atoms). The magnetization has an influence on the peak intensity, and the sensitivity decreases as B > C > D. Peak A is more sensitive to the magnetization states of the samples than other peaks (B, C, D). For the Ni K-edge, the peak intensities of E and F are not sensitive to the magnetization. A similar result was obtained in the XMCD for Fe–Co alloys by Pizzini et al. (1994
). They found a positive peak and negative structure at the Fe K-edge and only negative structure at the Co K-edge. The intensity of the negative peak in the Co K-edge XMCD decreases with Co concentration, which corresponds to an increase of the positive peak intensity in the Fe K-edge XMCD. In our case, Mn and Ni K-edge XMCD can be compared with Fe and Co XMCD in Fe–Co alloys, respectively. As the Mn concentration changes as 0.20, 0.24, 0.25, the intensity of the positive peak A in the Mn K-edge XMCD increases, but that of the negative peaks (E, F, G) in the Ni K-edge decreases.
![]() | Figure 2 (a) Peak intensities of A, B, C and D in magnetic XANES for the Mn K-edge (Fig. 1 ![]() ![]() |
On the band scheme, we can relate the positive peak A to the majority d-hole states near the which is supported by the fact that the 4p states are hybridized with the 3d states of the surrounding atoms. Within this interpretation, the decrease of the intensity of the positive peak A with increasing Ni concentration is in agreement with the decrease of the hole concentration of the majority d spin band on Mn. Pizzini et al. (1994) reported the increase of the in the Fe d-state as being due to the Fe concentration. Our results suggest that a d-hole exists only near the (peak A is sensitive to the Ni concentration) and the effect of the d state is small (peaks B, C, D are not so sensitive to the concentration) in the higher-energy region as discussed previously.
4.2. Magnetic for Ni0.76Mn0.24
In this section we discuss the Mn K-edge magnetic for Ni0.76Mn0.24 alloy. The reason why we study this concentration is that the ordered phase of Ni0.76Mn0.24 alloy is easily obtained using a shorter heat treatment than that of Ni0.75Mn0.25 alloy. It takes longer to form ordered Ni0.75Mn0.25 alloy and so residual oxygen can oxidize the sample. Magnetic is quite a powerful method for investigating the local magnetic structure, since this method has many advantages over the usual technique. Recent measurements of the magnetic have been reported for the alloys (Pizzini et al., 1994) and theoretical analyses have been applied to Fe–Co and Fe–Pt alloys (Popescu et al., 1999
).
Fig. 3(a) shows the oscillation function, kχ(k), for magnetic (solid line) and non-magnetic (dashed line) for the Mn K-edge of an Ni0.76Mn0.24 foil sample. The background subtraction is performed according to the XANADU code (Sakane et al., 1993
). The magnetic signal is normalized by an edge jump of the non-magnetic X-ray to unity. This figure shows that the magnetic includes higher-frequency components in comparison with the non-magnetic EXAFS.
![]() | Figure 3 (a) kχ(k) spectra for the Mn K-edge of Ni0.76Mn0.24 alloy. (b) Fourier transforms of the kχ(k) spectra for the Mn K-edge of Ni0.76Mn0.24 alloy. The solid line represents the magnetic and the dashed line represents the non-magnetic EXAFS. |
Fig. 3(b) shows the Fourier transforms of the kχ(k) shown in Fig. 3
(a). For the data analyses we used the XANADU code. The k-range of the Fourier transform is 2.0–10.8 Å−1. The solid line (dashed line) shows the result for the magnetic (non-magnetic) Vertical arrows in Fig. 3
(b) denote the crystallographic positions of nearest-neighbour atoms in the Ni–Mn f.c.c. lattice from the central Mn atom. The first-nearest-neighbour atoms are located at 2.54 Å, the second at 3.59 Å, the third at 4.5 Å and the fourth at 5.08 Å. In Fig. 3
(a) the phase-shift correction is not considered, so the peak position is not equal to these crystallographic data. The non-magnetic intensities simply reflect the number of surrounding atoms as previously reported (Nakahata et al., 1995
). On the other hand, in the magnetic the intensity is quite different from that in the non-magnetic The peak intensity of the second-nearest-neighbour peak at 3.58 Å in the magnetic is stronger than that for the first nearest neighbour at 2.54 Å in comparison with the non-magnetic This observation can be interpreted as follows: after the appropriate heat treatment the Ni–Mn alloys are ordered and this ordered phase mainly contributes to the In the ordered phase, the Mn atoms are expected to have large magnetic moments (
3.5 μB from neutron diffraction) in the second shell from the Mn atom. Therefore, the second nearest Mn atoms strongly contribute to the magnetic On the other hand, the third-shell atoms do not contribute to the magnetic because only Ni atoms exist as the third nearest neighbours.
Another characteristic feature is that the fourth-shell atoms give strong peaks in the magnetic 3Au-type ferromagnetic model. Idzerda et al. (1997) have reported that the higher-shell peaks are enhanced relative to the first-shell Fourier peak of the L-edge magnetic for Fe, Ni and Co in comparison with the non-magnetic In the present case, the strong peaks for the second and fourth shell could be explained as a result of enrichment of the Mn atoms.
In order to discuss the magnetic 3Mn including up to fourth-shell atoms (5 Å) around an X-ray-absorbing Mn atom. We have detailed information on the position of the atoms by X-ray diffraction and (Nakahata et al., 1995
; Miyanaga, Okazaki, Ikeda & Kon, 1999
). The lattice constant a = 3.59 Å (first-nearest-neighbour distance = 2.54 Å). In order to calculate the phase shift for the magnetic the electronic structures were obtained from the FLAPW method. As an example of a FLAPW calculation, the density of the structure is shown in Fig. 4
and the resulting electronic states are summarized in Table 1
. We used slightly modified electronic structures obtained from the FLAPW method for the phase-shifts calculation since the total charge is neutral in the Ni3Mn system. Fig. 5
(a) shows the calculated kχ(k) spectra of the Mn K-edge for the magnetic (solid line) and non-magnetic (dashed line) The calculated magnetic and non-magnetic predict the main features of the experimental result shown in Fig. 3
(a): the high-frequency component is more prominent in the magnetic than in the non-magnetic Fig. 5
(b) shows the Fourier transform of kχ(k) shown in Fig. 5
(a). The k-range for the Fourier transform is 2.0–10.8 Å−1 which is the same as for Fig. 3
(b). The amplitude of the calculated is larger than that for the experiment, which can be explained by thermal-vibration, electron mean-free-path and many-body effects neglected in the present analyses. In the theoretical XMCD spectra the second and the fourth peaks are also enhanced in Fig. 5
(b). This means that the 2NN and 4NN positions are replaced by Mn atoms due to the heat treatment (atomic ordering) as observed in the ordering of Ni3Mn alloy. Actually, previous analysis shows that the local structure around the Mn atom in ordered Ni0.80Mn0.20 is similar to that for ordered Ni3Mn (Babanov et al., 2001
). On the other hand, we find a prominent discrepancy between the experimental and theoretical results at the third- and fourth-nearest-neighbour peaks. The theoretical XMCD peak intensities are in the order second > third > fourth (Fig. 5
b). On the other hand, they are in the order fourth > second >> third (the third peak is not observed clearly) in the experimental result (Fig. 3
b). The following are reasons why the 4NN peak intensity is enhanced in the magnetic EXAFS:
![]() | Figure 4 Total density of states (DOS) calculated by the FLAPW method for the ordered Ni3Mn f.c.c. lattice model. The black shadow represents the states of the Mn atom, the grey shadow represents the states of the Ni atom, and the solid line represents the total contribution. |
![]() | Figure 5 (a) Calculated kχ(k) spectra for the Mn K-edge of ordered Ni3Mn alloy. (b) Fourier transforms of the calculated kχ(k) spectra for the Mn K-edge of the ordered Ni3Mn alloy model. The solid line represents the magnetic and the dashed line represents the non-magnetic EXAFS. |
(i) The focusing effect (or multiple scattering in the linearly arranged atoms) as observed in the normal
spectra. The peak intensity backscattered from the outer Mn atom in the Mn–Ni–Mn linear arrangement is enhanced by the photoelectron focusing effect. This effect is not taken into account in the present calculation of magnetic EXAFS.(ii) This phenomenon is generally observed in magnetic et al. (1997). Further systematic study is required to understand which effect is essential for the 4NN strong peaks in the magnetic for the Ni–Mn alloy.
5. Conclusion
Magnetic K-edge for Ni1−xMnx (x = 0.25, 0.24 and 0.20) show that: (i) local magnetic structure around the Mn atom is quite different from that around the Ni atom, and (ii) the peak intensity in the magnetic XANES of the Mn K-edge depends on the magnetization of the sample in contrast to the Ni K-edge. We also measured the Mn K-edge magnetic for Ni0.76Mn0.24. We observed that the second and fourth peaks in the Fourier transform are enhanced in comparison with the non-magnetic This means that the second- and fourth-shell Ni atoms are replaced by Mn atoms due to heat treatment (atomic ordering). Semi-relativistic theoretical calculations explain well the observed magnetic Experimental results show that the fourth peak is more prominent than expected by the theoretical calculation. Further study is necessary to explain the characteristic features of the fourth-shell peak in magnetic EXAFS.
spectra have been measured for Ni–Mn alloys. The XMCD of the Mn and NiAcknowledgements
The authors thank Dr M. Suzuki, Professor H. Maruyama, Dr T. Iwazumi, Dr Y. Watanabe and Dr T. Nakamura for kindly supporting the measurement of the magnetic
One of the authors (TM) thanks Professor Yu. A. Babanov and Professor A. Z. Menshikov for a fruitful discussion, and Professor E. D. Crozier for encouragement of this work. This work was performed under the approval of proposal No. 1998A0280NX-np of SPring-8 and proposals Nos. 98G236 and 2001G232 of the Photon Factory.References
Ankdinov, A. L. & Rehr, J. J. (1995). Phys. Rev. B, 52, 10214–10220. CrossRef Web of Science Google Scholar
Babanov, Yu. A., Crozier, E. D., Gordon, R. A., Miyanaga, T., Okazaki, T., Pilugin, V. P. & Ryazhkin, A. V. (2001). Nucl. Instrum. Methods Phys. Res. A, 470, 367–372. Web of Science CrossRef CAS Google Scholar
Brouder, Ch., Alouani, M. & Bennemann, K. H. (1996). Phys. Rev. B, 54, 7334–7349. CrossRef CAS Web of Science Google Scholar
Cable, J. W. & Child, H. R. (1974). Phys. Rev. B, 10, 4607–4615. CrossRef CAS Web of Science Google Scholar
Ebert, H. (1992). Jpn. J. Appl. Phys. 32, 299–301. CrossRef Google Scholar
Fujikawa, T. (1993). J. Phys. Soc. Jpn, 62, 2155–2165. CrossRef CAS Web of Science Google Scholar
Fujikawa, T., Hatada, K. & Hedin, L. (2000). Phys. Rev. B, 62, 5387–5398. Web of Science CrossRef CAS Google Scholar
Fujikawa, T., Hatada, K., Yikegaki, T. & Hedin, L. (1998). J. Electron Spectrosc. Relat. Phenom. 88/91, 649–655. Web of Science CrossRef Google Scholar
Fujikawa, T. & Nagamatsu, S. (2002). Jpn. J. Appl. Phys. 41, 2005–2013. Web of Science CrossRef CAS Google Scholar
Fujikawa, T., Yanagisawa, R., Yiwata, N. & Ohtani, K. (1997). J. Phys. Soc. Jpn, 66, 257–262. CrossRef CAS Web of Science Google Scholar
Gunnarsson, O. & Lundqvist, B. I. (1976). Phys. Rev. B, 13, 4274–4298. CrossRef CAS Web of Science Google Scholar
Hatada, K., Tanaka, H., Fujikawa, T. & Hedin, L. (2001). J. Synchrotron Rad. 8, 210–212. Web of Science CrossRef CAS IUCr Journals Google Scholar
Idzerda, Y. U., Chakarian, V. & Freeland, J. W. (1997). Synchrotron Rad. News, 10, 6–14. CrossRef Google Scholar
Iwazumi, T., Koyama, A. & Sakurai, Y. (1995). Rev. Sci. Instrum. 66, 1691–1693. CrossRef CAS Web of Science Google Scholar
Kobayashi, K., Maruyama, H., Iwazumi, T. & Yamazaki, H. (1996). Solid State Commun. 97, 491–496. CrossRef CAS Web of Science Google Scholar
Lovesey, S. W. & Collins, S. P. (1996). X-ray Scattering and Absorption by Magnetic Materials, pp. 151. Oxford: Clarendon Press. Google Scholar
Menshikov, A. Z. (1999). Private communication. Google Scholar
Miyanaga, T., Okazaki, T., Babanov, Yu. A. & Ryazhkin, A. (1999). Jpn. J. Appl. Phys. S38, 500–503. CrossRef Google Scholar
Miyanaga, T., Okazaki, T., Ikeda, S. & Kon, H. (1999). J. Magn. Soc. Jpn, 23, 620–622. CrossRef CAS Google Scholar
Nagamatsu, S. & Fujikawa, T. (2001). J. Synchrotron Rad. 8, 416–418. Web of Science CrossRef CAS IUCr Journals Google Scholar
Nakahata, M., Yuza, M., Kondo, Y., Miyanaga, T. & Okazaki, T. (1995). J. Phys. IV, 7(C2), 1185–1186. Google Scholar
Okazaki, T. (1995). Jpn. J. Appl. Phys. 34, 1537–1541. CrossRef CAS Web of Science Google Scholar
Paoletti, A. & Ricci, F. P. (1963). J. Appl. Phys. 34, 1571–1572. CrossRef Web of Science Google Scholar
Pizzini, S., Fontaine, A., Dartyge, E. C., Giorgetti, C. F., Baudelet, F., Kappler, J. P., Boher, P. & Giron, F. (1994). Phys. Rev. B, 50, 3779–3788. CrossRef CAS Web of Science Google Scholar
Popescu, V., Ebert, H. & Jenkins, C. (1999). J. Synchrotron Rad. 6, 711–713. Web of Science CrossRef CAS IUCr Journals Google Scholar
Ryazhkin, A., Babanov, Yu. A., Pilugin, V. P., Miyanaga, T., Okazaki, T., Crozier, E. D. & Gordon, R. A. (2001). J. Synchrotron Rad. 8, 300–301. Web of Science CrossRef CAS IUCr Journals Google Scholar
Sakane, H., Miyanaga, T., Watanabe, I., Matsubayashi, N., Ikeda, S. & Yokoyama, Y. (1993). Jpn. J. Appl. Phys. 32, 4641–4647. CrossRef CAS Web of Science Google Scholar
Sakurai, H., Itoh, F., Maruyama, H., Koizumi, A., Kobayashi, K. & Yamazaki, H. (1995). J. Phys. Soc. Jpn, 62, 459–463. CrossRef Web of Science Google Scholar
Sato, T., Goldfarb, R. B. & Patton, C. E. (1978). J. Appl. Phys. 49, 3439–3443. CrossRef Web of Science Google Scholar
Schutz, G., Wagner, W., Wilhelm, W., Kienle, P., Zeller, R., Frahm, R. & Materlik, G. (1987). Phys. Rev. Lett. 58, 737–740. CrossRef PubMed Web of Science Google Scholar
Suzuki, M., Kawamura, N., Mizumaki, M., Urata, A., Maruyama, H., Goto, S. & Ishikawa, T. (1999). J. Synchrotron Rad. 6, 190–192. Web of Science CrossRef CAS IUCr Journals Google Scholar
Yanase, A. (1995). Fortran Program for Space Group, 1st ed. Tokyo: Shokabo. (In Japanese.) Google Scholar
© International Union of Crystallography. Prior permission is not required to reproduce short quotations, tables and figures from this article, provided the original authors and source are cited. For more information, click here.