short communications
A new in situ cell for investigations
aInstitute of Inorganic and Analytical Chemistry, Justus Liebig University Giessen, Heinrich-Buff-Ring 58, D-35392 Giessen, Germany
*Correspondence e-mail: michael.froeba@anorg.chemie.uni-giessen.de
A new in situ cell for X-ray absorption spectroscopic investigations has been designed and tested. In contrast to existing cells, it is able to reach temperatures as high as 1250 K and can record X-ray absorption spectra in transmission and fluorescence modes. Furthermore, the cell is equipped with a new sample-holder system which allows an easy sample changing. All components are commercial and are simple to build. The cell is light and easy to handle, and can be used under reducing or oxidizing conditions which makes it suitable for performing reduction and oxidation investigations as demanded, e.g. in experiments. The cell was tested on the reduction of haematite.
1. Introduction
Interest in in situ experiments using X-ray absorption spectroscopy has been on the increase in recent years. The possibility of performing time- and temperature-resolved experiments has lead to the design of different in situ cells for several approaches (Jentoft et al., 2004; Ressler, 2003; Pettiti et al., 1999; van Bokhoven et al., 1999; Kampers et al., 1989; Dent et al., 1995; Zhang et al., 1991). Most of them are used in the study of catalysts (Ressler et al., 2003; Wienold et al., 2003).
Here we report on the construction of a new in situ cell with a wide range of applications. The cell is of a simple design – the use of special and complex manufactured parts has been avoided. All of the parts used are not expensive and can be assembled in a common machine shop. In addition, the cell is light, easy to handle and robust.
The sample-holder system was constructed for the housing of sample pills. It allows a very simple sample changing combined with a reproducible setting with respect to the sample position. The chosen material and design benefit the temperature distribution as well as gas changes during the measurements.
The most important advantage of the cell is the combination of several features known from other cells (e.g. high temperature without detection). The cell makes in situ studies possible for elements with an absorption of X-rays over a wide range. Simultaneous detection of transmission and is possible. During experiments the temperature can be varied from room temperature up to 1250 K. A wide choice of gas mixtures for reduction and oxidation cycles is conceivable.
2. In situ cell
The cell consists of three main parts: (i) the reaction room, which accommodates (ii) the sample holder, and (iii) the gas and temperature control system.
The main part of the reaction room is a T-shaped quartz tube (25 mm in diameter), around which are wrapped a heating wire and copper cooling tubes. An S-shape winding of the heating wire allows a nearly uniform temperature distribution at the sample position. In order to attach the wire and to gain a better temperature assignment the heating wire was built of oven cement. The area of constant temperature was estimated to be an area 7.5 mm × 7.5 mm around the sample position.
The ends of the tube are closed using brass flanges, which consist of an end cap, a spacer, a gasket and a screw holder. The end caps are bored 25 mm in diameter and equipped with an epoxy-sealed Kapton polyimide foil (of thickness 50 µm) for the X-ray beam to pass through. Changing the window material (e.g. to beryllium) is possible if necessary. Each of the two spacers is equipped with a tube for gas inlet or outlet. In addition, one spacer carries and fixes the thermocouple (Pt10%Rh/Pt), which is embedded in a ceramic tube, positioned such that its end is close to the sample position and at 2 mm from the quartz wall. The set-up is shown schematically in Fig. 1, and Figs. 2, 3 and 4 show different views of the entire cell. Important cell parameters are listed in Table 1.
|
First investigations show that it is possible to reduce the size of the entire cell by more than a half without restricting any of the features described above. This might be useful for space-restricted beamlines or for increasing the transmission and fluorescence yields.
The design and construction of this cell offers some technical and safety advantages, e.g. the structural separation between the electric (especially the heating area) and the water-cooling parts. In addition, the sample and the experimental gas are physically separated from the electric and heating wires.
The sample holder consists of a specially cut quartz tube as shown in Fig. 5. The sample, pressed as a boron nitride pellet (maximum diameter 16 mm), is mounted at an angle of 45° to the direction of the cut quartz tube. The quartz tube is specially cut to avoid any shielding of the fluorescence radiation. The reaction gas impinges on the sample after flowing through the tube. This makes it possible to switch gases while ignoring the gas mixture in the fluorescence arm of the cell.
In order to change the sample, one of the end caps has to be removed. The sample holder is then inserted into the furnace up to the desired position (marked on the outside) and the end cap is then replaced.
The in situ cell operates with a programmable temperature controller (Eurotherm 815S) with the possibility of performing heating ramps. The temperature allocations during these ramps are shown in Fig. 6. The temperature curves are recorded under real conditions (i.e. at the sample position with a nitrogen gas flow of 5 cm3 min−1, water cooling and aligned sample holder). It can be clearly seen that after a self-optimization procedure of the controller the differences between the desired and the real temperature are marginal over a large temperature range.
3. measurements
First tests were carried out at the HASYLAB@DESY EXAFSII beamline E4. The cell was tested in an experiment on the reduction of bulk haematite.
For the in situ measurements, bulk haematite was pressed into a boron nitride pellet of diameter 10 mm and thickness 0.5 mm. The reaction gas was 5% hydrogen in nitrogen with a flow rate of 5 cm3 min−1 and a heating rate of 2° min−1. spectra were recorded in a temperature range from 320 K up to 1150 K. It should be mentioned that the spectra were not collected in equidistant temperature steps. This is due to the different temperature ranges where a reduction to the respective iron oxides appears.
Figs. 7 and 8 show the corresponding energy-calibrated normalized background-corrected XANES spectra recorded at the Fe K edge in transmission and fluorescence mode, respectively. For both, a temperature-dependent change of the pre-edge peak is observed, combined with modifications in the white line and in the oscillations. Evaluation of the spectra using principle component analysis shows the appearance of four different phases for both the transmission and fluorescence spectra series. These phases are α-Fe2O3 (<570 K), Fe3O4 (570 K), FeO (640 K) and Fe0 (>1050 K), as expected (Webb & Orr, 1997). The proportions of the different iron phases in the transmission and fluorescence series are the same at respective temperatures. All these results demonstrate the usage of the in situ cell.
4. Conclusions
A new in situ cell has been designed, constructed and applied. It is able to reach temperatures up to 1250 K and can record X-ray absorption spectra in transmission and fluorescence modes. The sample holder allows for simple sample changing. The cell was successfully used in the reduction of haematite.
Acknowledgements
Financial support by the Fonds der Chemischen Industrie is gratefully acknowledged. We would like to thank HASYLAB@DESY for allocating beam time and the HASYLAB staff for supporting us. Thanks to Ralf Sack (head of our machine shop) for building the cell.
References
Bokhoven, J. A. van, van der Eerden, A. M. J., Smith, A. D. & Koningsberger, D. C. (1999). J. Synchrotron Rad. 6, 201–203. Web of Science CrossRef IUCr Journals
Dent, A. J., Greaves, G. N., Roberts, M. A., Sankar, G., Wright, P. A., Jones, R. H., Sheehy, M., Madill, D., Catlow, C. R. A., Thomas, J. M. & Rayment, T. (1995). Nucl. Instrum. Methods Phys. Res. B, 97, 20–22. CrossRef CAS Web of Science
Jentoft, R. E., Hahn, A. H. P., oft, F. C. & Ressler, T. (2004). Phys. Scr. Accepted.
Kampers, F. W. H., Maas, T. M. J., van Groundelle, J., Brinkgreve, P. & Koningsberger, D. C. (1989). Rev. Sci. Instrum. 60, 2635–2638. CrossRef Web of Science
Pettiti, I., Gazzoli, D., Inversi, M., Valigi, M., De Rossi, S., Ferraris, G., Porta, P. & Colonna, S. (1999). J. Synchrotron Rad. 6, 1120–1124. CrossRef CAS IUCr Journals
Ressler, T. (2003). Anal. Bioanal. Chem. 376, 584–593. Web of Science CrossRef PubMed CAS
Ressler, T., Wienold, J., Jentoft, R. E. & Girgsdies, F. (2003). Eur. J. Inorg. Chem. 2, 301–312. CrossRef
Webb, P. A. & Orr, C. (1997). Analytical Methods in Fine Particle Technology, p. 265. Norcross, GA: Micromeritics Instruments. (ISBN 0–9656783-0-X.)
Wienold, J., Timpe, O. & Ressler, T. (2003). Chem. Eur. J. 9, 6007–6017. Web of Science CrossRef PubMed CAS
Zhang, Z., Chen, H. & Sachtler, W. M. H. (1991). J. Chem. Soc. Faraday Trans. 87, 1413–1418. CrossRef CAS Web of Science
© International Union of Crystallography. Prior permission is not required to reproduce short quotations, tables and figures from this article, provided the original authors and source are cited. For more information, click here.