Figure 1
Diffraction patterns of ZrMo2O8 before (left, 0.32 GPa) and after (right, 1.64 GPa) the high-pressure transformation at 1.06–1.11 GPa. The light formation in the middle of the powder rings is the direct beam-stop. The single-crystal spot in the upper-right corner is due to the ruby crystal inserted for pressure measurements. |