short communications
![Open Access](/logos/open.png)
Comparing single-shot damage thresholds of boron carbide and silicon at the European XFEL
aEuropean XFEL, Holzkoppel 4, 22869 Schenefeld, Germany, bInstitute of Experimental Physics, Universitat Hamburg, Luruper Chaussee 149, 22761 Hamburg, Germany, cFZU – Institute of Physics, Czech Academy of Sciences, Na Slovance 2, 18221 Prague 8, Czechia, dDeutsches Elektronen-Synchrotron, Notkestrasse 85, 22607 Hamburg, Germany, eInstitute of Plasma Physics, Czech Academy of Sciences, Za Slovankou 3, 18200 Prague 8, Czechia, and fFaculty of Mathematics and Physics, Charles University, Ke Karlovu 3, 12116 Prague 2, Czechia
*Correspondence e-mail: marziyeh.tavakkoly@xfel.eu
This article forms part of a virtual special issue containing papers presented at the PhotonMEADOW2023 workshop.
Xray free-electron lasers (XFELs) enable experiments that would have been impractical or impossible at conventional X-ray laser facilities. Indeed, more XFEL facilities are being built and planned, with their aim to deliver larger pulse energies and higher peak 4C) coatings on polished silicon substrate were investigated using 1 keV photon energy, similar to the X-ray mirrors currently installed at the soft X-ray beamlines (SASE3). The purpose of this study is to compare the damage threshold of B4C and Si to determine the advantages, tolerance and limits of using B4C coatings.
While seeking to increase the pulse power, it is quintessential to consider the maximum pulse fluence that a grazing-incidence FEL mirror can withstand. To address this issue, several studies were conducted on grazing-incidence damage by soft X-ray FEL pulses at the European XFEL facility. Boron carbide (BKeywords: damage threshold; single-shot damage threshold; B4C coating; X-ray mirrors; XFEL.
1. Introduction
X-ray free-electron laser (XFEL) facilities have the capability to produce high-brightness X-rays, enabling novel experiments to be performed (Tschentscher et al., 2017). The optical components of XFEL beamlines, such as mirrors and crystals, are constantly exposed to extremely intense photon beams concentrated in an ultrashort (fs) – a situation that could easily cause irreversible damage to their surfaces, leading to compromised performance or to an unusable state altogether. A critical question therefore needs to be asked – what is the maximum pulse fluence that a grazing-incidence FEL mirror can withstand under continuous photon impingement with MHz repetition rate at an accelerator-based light source such as the European XFEL (EuXFEL).
To address this question, we conducted grazing-incidence damage experiments for uncoated silicon substrates and B4C coated substrates, using the EuXFEL facility and in particular its soft X-ray beamline at 1 keV photon energy. We chose silicon as the substrate and B4C as the surface coating as this combination is most commonly used at soft X-ray FELs beamlines (Mazza et al., 2012; Tavakkoly et al., 2022
). A higher damage threshold fluence for the B4C coating is expected due to its good thermal properties, high melting point, low density and high reflectivity.
Previous studies have explored the damage threshold of similar materials under various conditions. For instance, experiments with uncoated silicon under normal incidence at 10 keV reported a damage threshold fluence, Fth, of 0.78 µJ µm−2 (Koyama et al., 2015). At a grazing angle of 22 mrad and 0.9 keV, silicon exhibited an Fth of 0.014 µJ µm−2 (Krzywinski et al., 2018
). Another study at 5.5 keV and an incident grazing angle of 11.4 mrad found a threshold fluence of 0.052 µJ µm−2 (Koyama et al., 2016
). For bulk B4C at normal incidence and 0.83 keV photon energy, the threshold fluence was 0.027 µJ µm−2 (Hau-Riege et al., 2010
). Moreover, a 50 nm B4C coating on a silicon substrate at 7 keV and an incident grazing angle of 4 mrad exhibited a damage threshold of 24 µJ µm−2 (Aquila et al., 2015
).
In this paper, we investigate the damage threshold of uncoated silicon and B4C coating for a grazing-incident angle of 9 mrad. The results of these experiments will provide critical insights into the durability and performance limits of these materials under extreme conditions, which is essential for optimizing the design and operation of XFEL beamlines.
2. Experimental setup
The experiment was conducted at the Small Quantum Systems (SQS) instrument at the EuXFEL (Mazza et al., 2012). The facility delivered X-ray pulses with an average pulse energy of approximately 4.7 mJ and of 25 fs at a photon energy of 1 keV. The samples analyzed in this study were a polished silicon wafer without any coating and a similar silicon substrate coated with B4C. The samples' dimensions were 29.8 mm in length, 19.8 mm in width and 1830–1870 µm in thickness, with a 50 nm-thick B4C layer.
Samples were irradiated at a grazing angle of 9 mrad, which is typically used for B4C coated mirrors at soft X-ray beamlines. This angle is below the critical angle of 32 mrad at 1 keV (https://henke.lbl.gov/tmp/xray1041.dat).
The experimental setup is shown in Fig. 1. A gas attenuator was used to adjust the pulse energy and therefore the fluence. The maximum deliverable pulse energy to the samples was 1.8 mJ. An X-ray gas monitor (XGM) detector recorded the incident pulse energy for each damage measurement (Mazza et al., 2012
). The shot-to-shot pulse energy fluctuation was measured to be 5%.
![]() | Figure 1 Schematic of the experimental setup. AT: attenuator; XGM: X-ray gas monitor. |
A pair of Kirkpatrick–Baez (KB) optics was utilized to focus the beam, resulting in a spot size with an effective area of 1590 µm2. In this experimental setup, two cross chambers were used, one for the sample and the other, at 700 mm downstream from the first chamber, for the YAG screen. The YAG screen in the second chamber was used to track the direct beam and its reflection.
At each different attenuation settings, 43 damage measurements were taken at a grazing angle of 9 mrad. Fig. 2 illustrates a representative set of damaged craters.
![]() | Figure 2 Representative single-shot damage craters at 9 mrad grazing-incidence angle. (Left) Silicon. (Right) B4C. |
3. Analysis and results
In order to obtain the threshold fluence, the first step is to determine the corresponding energy for damage threshold (Dastjani Farahani et al., 2011; Koyama et al., 2015
). We measured the areas of the damaged spots in grazing-incidence irradiation for this purpose.
When the beam has a perfect Gaussian shape, we can determine the ; Aquila et al., 2013
). For non-Gaussian beams, the is determined by minimizing the mean-square distance between experimental data points and a function of the beam profile in a plot of normalized fluence against the beam area. The beam function is determined using the procedure described by Chalupský et al. (2009
, 2010
),
Here, S represents the area of the ablation contour, and f(S) denotes the normalized fluence. We measured the damaged area for each pulse energy. Fig. 3 presents a plot of normalized fluence versus measured damaged area, with the red curve depicting the beam profile.
![]() | Figure 3 Normalized fluence versus damaged area at 1 keV. Each damaged area was measured for every pulse energy, with the red curve representing the beam profile. (Top) Silicon with threshold energy of 261 µJ. (Bottom) B4C with of 549 µJ. |
As a result of our studies the determined threshold energies for silicon and B4C are 261 µJ and 549 µJ, respectively.
Finally, to retrieve the threshold fluence Fth, one needs to determine the beam effective area. According to Chalupský et al. (2010), the effective area Aeff is determined by a method of ablation imprints and is defined by a relation between fluence and pulse energy, F = Epulse/Aeff. It was found to be 1590 µm2. As a result, the threshold fluence (Fth = Eth/Aeff) is 0.16 µJ µm−2 for Si and 0.34 µJ µm−2 for B4C.
4. Conclusion
Single-shot damage measurements were conducted on Si and B4C-coated Si to determine the damage threshold fluences. At 1 keV with a 9 mrad grazing angle, below the critical angle, the damage threshold fluence was determined to be 0.16 µJ µm−2 for Si and 0.34 µJ µm−2 for B4C. As expected, B4C has a damage threshold approximately twice that of Si.
Acknowledgements
This research was conducted at SQS under proposal number 900332. The authors express their gratitude to the members of the XRO, SQS, SEC and FZU groups for their valuable assistance in the design and measurement of the samples, as well as their support during beam time. Open access funding enabled and organized by Projekt DEAL.
Conflict of interest
The authors declare no competing interests.
Data availability
The authors confirm that the data supporting the findings of this study are available within the article and its supplementary materials.
Funding information
This work was supported by the HIR3X – Helmholtz International Laboratory on Reliability, Repetition, Results at the most advanced X-ray Sources, and Deutsches Elektronen-Synchrotron. The Czech co-authors greatly appreciate financial support of their work at large-scale laser facilities provided by the Czech Ministry of Education, Youth and Sports (LM2023068).
References
Aquila, A., Ozkan, C., Sobierajski, R., Hájková, V., Burian, T., Chalupsky, J., Juha, L., Störmer, M., Ohashi, H., Koyama, T., Tono, K., Inubushi, Y., Yabashi, M., Sinn, H., Tschentscher, T., Mancuso, A. P. & Gaudin, J. (2013). Proc. SPIE, 8777, 87770H. CrossRef Google Scholar
Aquila, A., Sobierajski, R., Ozkan, C., Hájková, V., Burian, T., Chalupský, J., Juha, L., Störmer, M., Bajt, S., Klepka, M. T., Dłużewski, P., Morawiec, K., Ohashi, H., Koyama, T., Tono, K., Inubushi, Y., Yabashi, M., Sinn, H., Tschentscher, T., Mancuso, A. P. & Gaudin, J. (2015). Appl. Phys. Lett. 106, 241905. Web of Science CrossRef Google Scholar
Chalupský, J., Hájková, V., Altapova, V., Burian, T., Gleeson, A. J., Juha, L., Jurek, M., Sinn, H., Störmer, M., Sobierajski, R., Tiedtke, K., Toleikis, S., Tschentscher, Th., Vyšín, L., Wabnitz, H. & Gaudin, J. (2009). Appl. Phys. Lett. 95, 031111. Google Scholar
Chalupský, J., Krzywinski, J., Juha, L., Hájková, V., Cihelka, J., Burian, T., Vyšín, L., Gaudin, J., Gleeson, A., Jurek, M., Khorsand, A. R., Klinger, D., Wabnitz, H., Sobierajski, R., Störmer, M., Tiedtke, K. & Toleikis, S. (2010). Opt. Express, 18, 27836. Web of Science PubMed Google Scholar
Dastjani Farahani, S., Chalupsky, J., Burian, T., Chapman, H., Gleeson, A. J., Hajkoya, V., Juha, L., Jurek, M., Klinger, D., Sinn, H., Sobierajski, R., Störmer, M., Tiedtke, K., Toleikis, S., Tschentscher, T., Wabnitz, H. & Gaudin, J. (2011). Nucl. Instrum. Methods Phys. Res. A, 635, S39–S42. CrossRef CAS Google Scholar
Hau-Riege, S. P., London, R. A., Graf, A., Baker, S. L., Soufli, R., Sobierajski, R., Burian, T., Chalupsky, J., Juha, L., Gaudin, J., Krzywinski, J., Moeller, S., Messerschmidt, M., Bozek, J. & Bostedt, C. (2010). Opt. Express, 18, 23933. Web of Science PubMed Google Scholar
Koyama, T., Yumoto, H., Miura, T., Tono, K., Togashi, T., Inubushi, Y., Katayama, T., Kim, J., Matsuyama, S., Yabashi, M., Yamauchi, K. & Ohashi, H. (2016). Rev. Sci. Instrum. 87, 051801. Web of Science CrossRef PubMed Google Scholar
Koyama, T., Yumoto, H., Tono, K., Togashi, T., Inubushi, Y., Katayama, T., Kim, J., Matsuyama, S., Yabashi, M., Yamauchi, K. & Ohashi, H. (2015). Proc. SPIE, 9511, 951107. Google Scholar
Krzywinski, J., Conley, R., Moeller, S., Gwalt, G., Siewert, F., Waberski, C., Zeschke, T. & Cocco, D. (2018). J. Synchrotron Rad. 25, 85–90. CrossRef CAS IUCr Journals Google Scholar
Liu, J.-M. (1982). Opt. Lett. 7, 196. CrossRef PubMed Google Scholar
Mazza, T., Zhang, H. & Meyer, M. (2012). Technical Design Report: Scientific Instrument SQS, Report XFEL.EU TR-2012–007. EuXFEL, Hamburg, Germany. Google Scholar
Tavakkoly, M., Grünert, J., Koch, A., La Civita, D., Makita, M., Meyer, M., Planas, M., Serkez, S., Sinn, H., Wohlenberg, T. & Vannoni, M. (2022). J. Phys. Conf. Ser. 2380, 012066. CrossRef Google Scholar
Tschentscher, T., Bressler, C., Grünert, J., Madsen, A., Mancuso, A., Meyer, M., Scherz, A., Sinn, H. & Zastrau, U. (2017). Appl. Sci. 7, 592. Web of Science CrossRef Google Scholar
This is an open-access article distributed under the terms of the Creative Commons Attribution (CC-BY) Licence, which permits unrestricted use, distribution, and reproduction in any medium, provided the original authors and source are cited.
![Open Access](/logos/open.png)